ACCUTECH™ NY0730G40L
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | ACLO Compounders Inc. |
| Trademark: | ACCUTECH™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IcI3vA_ACCUTECH-NY0730G40L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ACCUTECH™ NY0730G40L is a Polyamide 6 (Nylon 6) product filled with 40% glass fiber. It is available in North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 3.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.10 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 109 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4600 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 170 | MPa | |
| Break | 170 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield | 5.0 | % | |
| Break | 7.0 | % | |
| Flexural Modulus | 11300 | MPa | ASTM D790 |
| Flexural Strength | 263 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 180 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 200 | °C | ASTM D648 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Toppyl SP 2000 B | LyondellBasell Industries | Polyolefin, Unspecified | Toppyl |
| Braskem PP CP1200B | Braskem America Inc. | PP Homopolymer | Braskem PP |
| GELOY™ XP4025 resin | SABIC Innovative Plastics | ASA+PC | GELOY™ |
| GLAMIDE® NB-5620S | TOYOBO America, Inc. | Nylon, Unspecified | GLAMIDE® |
| Hanwha Total PP EX17 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, HMS | Hanwha Total PP |