VECTRA® A950
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | VECTRA® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ib3NFW_VECTRA-A950.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Unreinforced Vectra grade suitable for extrusion. Chemical abbreviation according to ISO 1043-1 : LCP Inherently flame retardant FDA compliant. UL-Listing V-0 in natural and black at 0.42mm thickness per UL 94 flame testing. Relative-Temperature-Index (RTI) according to UL 746B: electrical 240°C, mechanical 220°C. UL = Underwriters Laboratories (USA) |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Multi-Point Data |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.40 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.70 | % | ISO 294-4 |
| Flow direction | 0.0 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 6.0E-3 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 3.0E-3 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10600 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 182 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 3.4 | % | ISO 527-2/1A/5 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 9000 | MPa | ISO 899-1 |
| 1000 hr | 6600 | MPa | ISO 899-1 |
| Flexural Modulus (23°C) | 9100 | MPa | ISO 178 |
| Flexural Stress (23°C) | 158 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 95 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 53 | kJ/m² | ISO 179/1eU |
| 23°C | 270 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 95 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 250 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, not annealed | 187 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 94.0 | °C | ISO 75-2/C |
| Vicat Softening Temperature | 145 | °C | ISO 306/B50 |
| Melting Temperature 1 | 280 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 4.0E-6 | cm/cm/°C | ISO 11359-2 |
| Lateral | 3.8E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | 47 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 3.20 | IEC 60250 | |
| 1 MHz | 3.00 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 0.016 | IEC 60250 | |
| 1 MHz | 0.020 | IEC 60250 | |
| Comparative Tracking Index | 150 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Hopper Temperature | 20.0 - 30.0 | °C | |
| Rear Temperature | 270 - 280 | °C | |
| Middle Temperature | 275 - 285 | °C | |
| Front Temperature | 280 - 290 | °C | |
| Nozzle Temperature | 290 - 300 | °C | |
| Processing (Melt) Temp | 285 - 295 | °C | |
| Mold Temperature | 80.0 - 120 | °C | |
| Injection Pressure | 50.0 - 150 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 - 150 | MPa | |
| Back Pressure | 0.00 - 3.00 | MPa | |
| Screw Speed | 80 - 200 | rpm |
| Injection instructions |
|---|
| Zone 4 Temperature: 285 to 295°CManifold Temperature: 285 to 295°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 207.3F | RTP Company | Nylon 12 | RTP |
| Hanwha Total PE PE20 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | EVA | Hanwha Total PE |
| Karina GREEN PVC COMPOUND 700D40/356-AT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Hifax X M2 U16 C11544 | LyondellBasell Industries | PP Homopolymer | Hifax |
| TEDUR® L FC 9510-6 | ALBIS PLASTIC GmbH | PPS | TEDUR® |