Vipel® K733-BPT-20
| Category: | Polyester Alloy , Polyester Alloy |
| Manufacturer: | AOC, L.L.C. |
| Trademark: | Vipel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IauNIu_Vipel-K733-BPT-20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Firepel® Polyester Resin for Filled Fire Retardant Applications AOC's Firepel® K320-A series are promoted, non thixotropic resins specifically designed to be blended with alumina trihydrate (ATH) to provide fire retardant properties. ATH is needed to provide fire retardant properties. Firepel® K320-A series resins are used for mass transit applications. Flammability of composite parts is dependent on the geometry of the part, degree of cure, reinforcement content, types of reinforcement, etc. It is the end user's responsibility to ensure that finished parts meet the required specifications. Published flammability properties should be used for comparison purposes only. Fire Resistance Firepel® K320-A series resins are designed for use in filled applications where fire retardancy and low smoke emissions are required. Toxicity Composites made with Firepel® K320- A series resins have low toxicity values due to the absence of halogens. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | |
| Styrene Content | 39 | % |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Spread Index 1 | 15.0 | ASTM E84 | |
| Smoke Developed 2 | 650 | ASTM E84 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Exotherm | |||
| Gel to Peak | 6.0 | min | |
| Peak | 179 | °C | |
| Gel Time (25°C) 3 | 20.0 | min |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Thixotropic Index 4 | 2.00 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Barcol Hardness | 44 | ASTM D2583 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3790 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 75.8 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.4 | % | ASTM D638 |
| Flexural Modulus | 4000 | MPa | ASTM D790 |
| Flexural Strength | 124 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 96.1 | °C | ASTM D648 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Mix Viscosity 5(25°C) | 450 | cP |
| Note Message | |
|---|---|
| 1 . | 1.5% Antimony Trioxide |
| 2 . | 1.5% Antimony Trioxide |
| 3 . | Gel time with 1.25% MEKP |
| 4 . | 2/20 rpm Thix Index |
| 5 . | Brookfield RV viscosity spindle 2 at 20 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2285 LF TFE 15 Z | RTP Company | PEEK | RTP |
| RTP EMI 330B FR | RTP Company | PC | RTP |
| BITONER® C9 BA-120 | Qingdao Bater Chemical Co., Ltd. | TP, Unspecified | BITONER® |
| Formolene® 6510E | Formosa Plastics Corporation, U.S.A. | PP Impact Copolymer | Formolene® |
| TECACOMP® PEEK 450 CF30 black 3198 | Ensinger GmbH | PEEK | TECACOMP® |