AVP™ RYY13CP
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | AVP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IagfuH_AVP-RYY13CP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| AVP™ RYY13CP is a Polyamide 66 (Nylon 66) product filled with 13% glass fiber. It can be processed by injection molding and is available in North America. Primary characteristic: heat stabilizer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.40 to 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Ultimate, 3.18 mm) | 103 | MPa | ASTM D638 |
| Flexural Modulus 2(3.18 mm, 50.8 mm Span) | 4480 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 37 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.35 mm) | 232 | °C | ASTM D648 |
| Melting Temperature | 249 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Shot Size | 40 to 80 | % | |
| Rear Temperature | 249 to 282 | °C | |
| Middle Temperature | 260 to 288 | °C | |
| Front Temperature | 271 to 304 | °C | |
| Nozzle Temperature | 271 to 304 | °C | |
| Processing (Melt) Temp | 271 to 304 | °C | |
| Mold Temperature | 65.6 to 110 | °C | |
| Back Pressure | 0.172 to 1.03 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.1 mm/min |
| 2 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SolVin 266SC | INOVYN | PVC, Unspecified | SolVin |
| Synprene™ RT-5190 RoHS Black | PolyOne Corporation | SBC | Synprene™ |
| MAJORIS ET217 | AD majoris | PP, Unspecified | MAJORIS |
| Perlast® G75S | Precision Polymer Engineering Ltd. | Perfluoroelastomer | Perlast® |
| Plexar® PX1164 | LyondellBasell Industries | EVA | Plexar® |