TAROMID B 280 G4 X0
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROMID B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IZHPgT_TAROMID-B-280-G4-X0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polyamide 6 glass fiber reinforced 20%, UL94 V0 self extinguishing, good flame proofing also at low thickness, good flow and good mechanical properties. UL94 V0 approuved all colors at 0,97 mm. UL746B approved. Available: different colors, heat stabilized (H), release agent (W), and without PBDE/PBDF. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 to 1.42 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.30 to 0.50 | % | |
| Across Flow | 0.50 to 0.80 | % | |
| Water Absorption | |||
| 23°C, 24 hr | 1.5 | % | ASTM D570, ISO 62 |
| Saturation | 7.0 | % | ASTM D570 |
| Saturation, 23°C | 7.0 | % | ISO 62 |
| Granule Humidity | < 0.10 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7000 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Break) | 120 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 6500 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 150 | MPa | ISO 178 |
| Break | 150 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 1(23°C) | 5.8 | kJ/m² | ASTM D256, ISO 179 |
| Notched Izod Impact (23°C, 3.20 mm) | 60 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 200 | °C | ASTM D648, ISO 75-2/A |
| Continuous Use Temperature | IEC 60216 | ||
| -- 2 | 90.0 | °C | |
| -- 3 | 120 | °C | |
| -- 4 | 130 | °C | |
| -- 5 | 160 | °C | |
| Vicat Softening Temperature | |||
| -- | 210 | °C | ASTM D1525, ISO 306/A50 8 6 |
| -- | 205 | °C | ASTM D1525, ISO 306/B50 9 7 |
| Ball Pressure Test (165°C) | Pass | VDE 0470 | |
| Melting Temperature | 222 | °C | ASTM D211, ISO 121 |
| CLTE - Flow (-30 to 30°C) | 3.8E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Comparative Tracking Index (Solution A) | 300 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.970 mm) | V-0 | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 960 | °C | IEC 60695-2-13 |
| Oxygen Index | 30 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 to 90.0 | °C | |
| Pre-heater | 80.0 to 100 | °C | |
| Drying Time | |||
| -- | 1.0 | hr | |
| Pre-heater | 3.0 | hr | |
| Processing (Melt) Temp | 230 to 250 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 6x4x50 mm |
| 2 . | 20000 hrs |
| 3 . | Heat Stabilized, 20000 hrs |
| 4 . | Short Term |
| 5 . | Heat Stabilized, Short Term |
| 6 . | Rate A (50°C/h), Loading 1 (10 N) |
| 7 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecnoflon® FOR TF 636 | Solvay Specialty Polymers | Fluorelastomer | Tecnoflon® |
| Akulon® S223-PG8 | DSM Engineering Plastics | Nylon 66 | Akulon® |
| Cri-Line LC-815-85-THK | Cri-Tech, Inc. | Fluorelastomer | Cri-Line |
| Karina BLACK PVC COMPOUND -E 880-48/ 1-E-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUBEMID A26 GK50 NATURAL | LUBEN PLAST srl | Nylon 66 | LUBEMID |