Radilon® S EGR1404 990 GRI
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Radici Plastics |
| Trademark: | Radilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IZ0p0v_Radilon-S-EGR1404-990-GRI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PA6 injection moulding grade. Very low friction. Natural grey colour. Suitable for parts and components requiring low friction and improved wear resistance such as gears, bearings, and cams. Typical application: interchangeable sectors for pulleys. ISO 1043 : PA6-I |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.17 | -- | g/cm³ | ISO 1183 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3100 | -- | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 65.0 | -- | MPa | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | 17 | -- | % | ISO 527-2/1A/50 |
| Flexural Modulus 1 | 2800 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 100 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | -- | kJ/m² | ISO 179/1eA |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 85.0 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 180 | -- | °C | ISO 306/B50 |
| Melting Temperature 3 | 220 | -- | °C | ISO 11357 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | < 30 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 80.0 | °C | |
| Drying Time - Desiccant Dryer | 2.0 to 4.0 | hr | |
| Dew Point - Desiccant Dryer | < -20.0 | °C | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 250 to 280 | °C | |
| Mold Temperature | 70.0 to 80.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DILAMID® 66 FVT 35 NAT A | Dilaplast S.p.A. | Nylon 66 | DILAMID® |
| Elastron® G G601.A90.B | Elastron USA, Inc. | SEBS | Elastron® G |
| ICORENE® 4035 | ICO Polymers EMEA, A Division of A. Schulman | PP Impact Copolymer | ICORENE® |
| Karina STRAW PVC COMPOUND -E 520-38/ 24-B | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| EPITEC® PC-910FH | Osterman & Company | PC | EPITEC® |