Infino HM-1100F
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IVZG4U_InfinoHM1100F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Infino HM-1100F is a polycarbonate acrylonitrile butadiene styrene (PC ABS) product, which contains a glass fiber reinforced material. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: electrical/electronic applications. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.25 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238, ISO 1133 | ||
| 220°C/10.0 kg | 26 | g/10 min | ASTM D1238, ISO 1133 |
| 250°C/2.16 kg | 8.0 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20mm | 0.10 - 0.20 | % | ASTM D955 |
| Transverse flow : 3.20mm | 0.10 - 0.20 | % | ASTM D955 |
| Lateral flow : 3.20mm | 0.10 - 0.20 | % | ISO 2577 |
| Traffic : 3.20mm | 0.10 - 0.20 | % | ISO 2577 |
| Tg (half width) - DSC | 98 | °C | |
| Ash Content | |||
| -- | 11 | % | ISO 3451 |
| -- | 10 | % | ASTM D5630 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 118 | ASTM D785 | |
| R scale | 118 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3400 | MPa | ASTM D638 |
| -- | 3400 | MPa | ISO 527-2/5 |
| Tensile Strength | |||
| Yield 2 | 78.0 | MPa | ASTM D638 |
| Yield | 80.0 | MPa | ISO 527-2/5 |
| Fracture 3 | 78.0 | MPa | ASTM D638 |
| Fracture | 85.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Fracture 4 | 5.0 | % | ASTM D638 |
| Fracture | 4.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| -- 5 | 3900 | MPa | ASTM D790 |
| -- 6 | 4000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 98.0 | MPa | ASTM D790 |
| -- 8 | 100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 7.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 79 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 79 | J/m | ASTM D256 |
| 23°C 10 | 8.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 6.40mm | 95.0 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 4.00mm | 95.0 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 6.40mm | 94.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed, 4.00mm | 94.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 98.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 2.0 mm | V-0 | UL 94 | |
| 2.5 mm | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4mm |
| 10 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom SC7-70915 | Spartech Polycom | PC | Spartech |
| TORZEN® G3500HSL BK20 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |
| Jam PE 52518 | Jam Petrochemical Company | HDPE | Jam PE |
| LNP™ LUBRICOMP™ RVL29XXP compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ LUBRICOMP™ |
| Sylvin 6227-95 Purple 8457 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |