TECAMID™ MDS
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Ensinger Inc. |
| Trademark: | TECAMID™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IV5Ya2_TECAMID-MDS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Nylon is one of the most widely used and versatile thermoplastic resins. Its combination of physical properties versus its price makes it a favorite choice for numerous applications. Nylon has a consistent history of replacing other materials including: metal, brass, bronze, aluminum, and rubber. In replacing metal gears in machinery, nylon can be advantageous because of its ability to reduce noise, use less lubrication and increase gear life. TECAMID® MDS is an extruded "moly" filled nylon 6/6, which is gray in color. The addition of particles of molybdenum disulfide enhances the surface lubricity and wear resistance over unfilled nylon. In applications requiring high lubricity, this material may be a good candidate. In addition to the greater lubricity there are many additional property enhancementsthat occur. TECAMID® MDS has enhanced properties which make it an ideal material to replace metals in machinery. It can increase the life of many moving parts as well as provide a noise reduction benefit and requires less lubrication. A very stable compound with many industrial applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Water Absorption | ASTM D570 | ||
| 23°C, 24 hr | 1.2 - 2.5 | % | ASTM D570 |
| Saturated, 23°C | 7.5 - 8.5 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale, 23°C) | 87 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3100 | MPa | ASTM D638 |
| Tensile Strength (Yield, 23°C) | 75.8 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 15 | % | ASTM D638 |
| Flexural Modulus (23°C) | 3100 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 117 | MPa | ASTM D790 |
| Wear Factor 1(0.28 MPa, 0.25 m/sec) | 380 | 10^-8 mm³/N·m | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (23°C) | 64 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 243 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 90.0 | °C | ASTM D648 |
| Peak Melting Temperature | 255 | °C | ASTM D3418 |
| CLTE - Flow | 7.2E-5 | cm/cm/°C | ASTM D696 |
| Specific Heat | 1670 | J/kg/°C | |
| Maximum Service Temperature | |||
| Intermittent | 179 | °C | |
| Long Term | 110 | °C | UL 746B |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 1.2 | kV/mm | ASTM D149 |
| Dielectric Constant 2(23°C, 60 Hz) | 2.50 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information |
|---|
| Data obtained from extruded shapes material. |
| Note Message | |
|---|---|
| 1 . | Against Steel |
| 2 . | 50% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 TFE 20 SI 5 | RTP Company | Nylon 66 | RTP |
| SABIC® HDPE M30053S | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® HDPE |
| Witcom PBT 6G/2L3 | Witcom Engineering Plastics B.V. | PBT | Witcom PBT |
| DOW™ Electrical & Telecommunications HFDB-4201 SC K | The Dow Chemical Company | XLPE | DOW™ Electrical & Telecommunications |
| INVISION™ GX 5080G2F | A. Schulman Inc. | TPE | INVISION™ |