Hanwha Total PP BI300
| Category: | PP, High Crystal , High Crystallinity Polypropylene |
| Manufacturer: | HANWHA TOTAL PETROCHEMICALS Co., Ltd. |
| Trademark: | Hanwha Total PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IUTi4v_Hanwha-Total-PP-BI300.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| BI300 is a high isotactic Block Copolymer which has higher crystallinity, compared to general PP. Due to high crystalline nature & optimum rubber design, BI300 has an excellent property balance between high stiffness and impact strength. Films made from this grade provide high heat resistance and superior mechanical strength, thus this grade is highly suited to retort pouch film application. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 81 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 23.5 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 500 | % | ASTM D638 |
| Flexural Modulus 3 | 1470 | MPa | ASTM D790 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 60 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 60 µm | 22.6 | MPa | ASTM D882 |
| TD : Yield, 60 µm | 20.6 | MPa | ASTM D882 |
| MD : Break, 60 µm | 53.0 | MPa | ASTM D882 |
| TD : Break, 60 µm | 36.3 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 60 µm | 700 | % | ASTM D882 |
| TD : Break, 60 µm | 700 | % | ASTM D882 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 0°C | 29 | J/m | ASTM D256 |
| 5°C | 39 | J/m | ASTM D256 |
| 23°C | 64 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 110 | °C | ASTM D648 |
| Vicat Softening Temperature | 155 | °C | ASTM D1525 4 |
| Melting Temperature | 163 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (60.0 µm) | 28 | % | ASTM D1003 |
| Additional Information |
|---|
| Izod Impact Strength, ASTM D3420: 3000 kg-cm/cm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| BMC 300 | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| Chemlon® MDF4L | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| Edgetek™ ES-30GF/000 Black | PolyOne Corporation | PESU | Edgetek™ |
| LUVOCOM® 3-8266/BL | Lehmann & Voss & Co. | Nylon 6 | LUVOCOM® |
| POLYform C M90 K5 | Polykemi AB | Acetal (POM) Copolymer | POLYform C |