Lucel® N109LD
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lucel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ITGsi9_Lucel-N109LD.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lucel® N109LD is an Acetal (POM) Copolymer material. It is available in Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of Lucel® N109LD are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 9.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 1.8 to 2.1 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 82 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 61.2 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 65 | % | ASTM D638 |
| Flexural Modulus 3(6.40 mm) | 2570 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 6.40 mm) | 89.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.40 mm) | 69 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 160 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 110 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| Volume Resistivity (23°C) | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C, 1.00 mm) | 24 | kV/mm | ASTM D149 |
| Dissipation Factor (1 MHz) | 3.8E-4 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.710 mm | HB | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 110 | °C | |
| Drying Time | 3.0 to 6.0 | hr | |
| Minimum Moisture Content | 0.10 | % | |
| Rear Temperature | 160 to 180 | °C | |
| Middle Temperature | 180 to 200 | °C | |
| Front Temperature | 190 to 200 | °C | |
| Nozzle Temperature | 190 to 200 | °C | |
| Processing (Melt) Temp | 190 to 200 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Back Pressure | 0.394 to 0.789 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 10 mm/min |
| 2 . | 10 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.8 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2300 A UV | RTP Company | TPU-Polyester | RTP |
| Andur 2-60 DP | Anderson Development Company | PUR-Ether/TDI | Andur |
| CYCOLOY™ CM4300 resin | SABIC Innovative Plastics Europe | PC+ABS | CYCOLOY™ |
| Lion Idemitsu Composites PPS Y531F1 | Lion Idemitsu Composites Co., Ltd. | PPS | Lion Idemitsu Composites PPS |
| Braskem PP DH765.01 | Braskem Europe GmbH | PP Homopolymer | Braskem PP |