Order Products : sales@su-jiao.com
Latan 13 K/30
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latan |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IT7cSB_Latan-13-K-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polyoximethylene (POM). Carbon fibre. Medium viscosity. Good tribological properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.50 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 1.0 to 1.3 | % | |
| Flow : 2.00 mm | 0.30 to 0.55 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 18500 | MPa | |
| 60°C | 14500 | MPa | |
| 90°C | 10000 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Break, 23°C | 120 | MPa | |
| Break, 60°C | 100 | MPa | |
| Break, 90°C | 65.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Break, 23°C | 0.90 | % | |
| Break, 60°C | 1.1 | % | |
| Break, 90°C | 1.2 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 2.0 | kJ/m² | |
| 23°C | 2.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 15 | kJ/m² | |
| 23°C | 15 | kJ/m² | |
| Notched Izod Impact (23°C, 3.20 mm) | 35 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 170 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 160 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 85.0 | °C | |
| Vicat Softening Temperature | 165 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 1.0E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 180 to 210 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® Vestolen A 6060R 65306 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® Vestolen A |
| Ultraform® N 2320 FC Aqua UN | BASF Corporation | Acetal (POM) Copolymer | Ultraform® |
| Adell Polyamide BT-33 | Adell Plastics, Inc. | Nylon 6 | Adell Polyamide |
| Adflex X 100 G | LyondellBasell Industries | TPO (POE) | Adflex |
| Di-Pak™ E-4596 | Hapco Inc. | TP, Unspecified | Di-Pak™ |