Clariant Nylon 6/6 66G33-L
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Clariant Corporation |
| Trademark: | Clariant Nylon 6/6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ISGwI6_Clariant-Nylon-6-6-66G33-L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Clariant Nylon 6/6 66G33-L is a Polyamide 66 (Nylon 66) material filled with 33% glass fiber. It is available in North America for injection molding. Important attributes of Clariant Nylon 6/6 66G33-L are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 145 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 8270 | MPa | ASTM D790 |
| Flexural Strength | 193 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 64 | J/m | ASTM D256 |
| Tensile Impact Strength | 58.8 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 253 | °C | |
| 1.8 MPa, Unannealed | 248 | °C | |
| Melting Temperature | 257 | °C | |
| RTI Elec | UL 746 | ||
| 1.57 mm | 105 | °C | |
| 3.18 mm | 110 | °C | |
| 6.10 mm | 110 | °C | |
| RTI Imp | UL 746 | ||
| 1.57 mm | 65.0 | °C | |
| 3.18 mm | 65.0 | °C | |
| 6.10 mm | 65.0 | °C | |
| RTI Str | UL 746 | ||
| 1.57 mm | 105 | °C | |
| 3.18 mm | 110 | °C | |
| 6.10 mm | 110 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.57 mm | HB | ||
| 3.18 mm | HB | ||
| 6.10 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 to 82.2 | °C | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 249 to 271 | °C | |
| Middle Temperature | 271 to 288 | °C | |
| Front Temperature | 282 to 299 | °C | |
| Nozzle Temperature | 266 to 288 | °C | |
| Mold Temperature | 71.1 to 104 | °C | |
| Injection Pressure | 55.2 to 138 | MPa | |
| Back Pressure | 0.00 to 1.03 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Santoprene™ 201-87 | ExxonMobil Chemical | TPV | Santoprene™ |
| Andur 8-6 APSLM/Curene® 442 | Anderson Development Company | PUR-Ester/TDI | Andur |
| EverGlide® SG5708T | Polymer Dynamix | PEEK | EverGlide® |
| DINAPLEN® PPH1S07 G20V0-4137 | Grupo Repol | PP Homopolymer | DINAPLEN® |
| Iupiace® GV20 | Mitsubishi Engineering-Plastics Corp | PPE+PS | Iupiace® |