LUBEMID A26 NATURAL HS
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LUBEN PLAST srl |
| Trademark: | LUBEMID |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ISErbF_LUBEMID-A26-NATURAL-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Compound based on PA66 natural first choice. Lubricated. Heat stabilized. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.11 to 1.15 | g/cm³ | ISO 1183/A |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2500 to 3000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | ISO 527-2/1A/50 | ||
| Yield | 60.0 to 65.0 | MPa | |
| Break | 60.0 to 65.0 | MPa | |
| Tensile Strain | ISO 527-2/1A/50 | ||
| Yield | 5.0 to 8.0 | % | |
| Break | 5.0 to 8.0 | % | |
| Flexural Modulus 1 | 1800 to 2300 | MPa | ISO 178 |
| Flexural Stress 2 | 65.0 to 70.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.5 to 4.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 40 to 60 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | |||
| 23°C, 3.20 mm | 30 to 50 | J/m | ASTM D256A |
| 23°C 3 | 80 to 90 | kJ/m² | ASTM D256 |
| 23°C | 2.5 to 4.5 | kJ/m² | ISO 180/A |
| 23°C 4 | 3.0 to 5.0 | kJ/m² | ASTM D256 |
| Unnotched Izod Impact Strength (23°C) | 50 to 70 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 215 to 225 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 220 to 230 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 3.20 mm | 70.0 to 80.0 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 240 to 250 | °C | ISO 306/A120 |
| -- | 230 to 240 | °C | ISO 306/B120 |
| Melting Temperature | 250 to 265 | °C | Internal Method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.20 mm) | V-2 | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 850 | °C | IEC 60695-2-12 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Notch E |
| 4 . | Notch A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMATOP PP CO 002-12 RC | Amco Polymers | PP Random Copolymer | PRIMATOP |
| SCANAMID 66 A53^EM | Polykemi AB | Nylon 66 | SCANAMID 66 |
| NEXUS PS 740 | Nexus Resin Group, LLC. | PS (HIPS) | NEXUS PS |
| Allen ABS AX7 | SEKISUI Polymer Innovations, LLC | ABS | Allen ABS |
| Elastoprene HS5060A NAT | KMI Group, Inc. | TPE | Elastoprene |