Order Products : sales@su-jiao.com
TOTAL Polystyrene 853S
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polystyrene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IQdzi7_TOTAL-Polystyrene-853S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polystyrene Compound 853S is a V2 non-halogenated flame retardant, high impact polystyrene for injection molding application. It is recommended for manufacturing of articles which require good dimensional stability. Applications:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Apparent Density | 0.60 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 4.0 | g/10 min | ASTM D1238, ISO 1133 |
| Spiral Flow 1 | 40.0 | cm | ASTM D3123 |
| Molding Shrinkage - Flow | 0.40 - 0.70 | % | ASTM D955 |
| Water Absorption | |||
| 24 hr | < 0.10 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | < 0.10 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Grade R, 23°C, Injection Molding | 93 | ASTM D785 | |
| R scale, 23°C | 93 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C, Injection Molded) | 28.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break, 23°C, Injection Molded) | 40 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus (23°C, Injection Molded) | 2200 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C, injection molding | 64 | J/m | ASTM D256 |
| 23°C, injection molding | 7.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 92.0 | °C | ISO 306/A50, ASTM D1525 2 |
| CLTE - Flow | 8.9E-5 | cm/cm/°C | ASTM D696 |
| Heat Distortion | |||
| -- | 75 | °C | ASTM D648 |
| -- | 75 | °C | ISO 75-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | IEC 60093 |
| Dielectric Strength | 160 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 190 - 210 | °C | |
| Middle Temperature | 210 - 230 | °C | |
| Front Temperature | 220 - 250 | °C | |
| Nozzle Temperature | 250 - 280 | °C |
| Injection instructions |
|---|
| Zone 4 Temperature: 250 to 260°C |
| Note Message | |
|---|---|
| 1 . | Melt temperature: 220°C |
| 2 . | 速率 A (50°C/h), 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Dryflex® 660600S | ELASTO | SEBS | Dryflex® |
| Generic Acetal (POM) Copolymer - Glass Bead | Generic | Acetal (POM) Copolymer | Generic |
| Kpren 135A | Shandong Xuye New Materials Co., Ltd. | CPE | Kpren |
| LOXIM 811 02T HB | LOXIM Industries Private Limited | PP Copolymer | LOXIM |
| Osterlene® LDC1821SA | Osterman & Company | LDPE | Osterlene® |