Shuang-Bang AB-6060

Category:	PUR, Unspecified , Polyurethane
Manufacturer:	Shuang-Bang Industrial Corp.
Trademark:	Shuang-Bang
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	IQViKn_Shuang-Bang-AB-6060.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
One component PU Resins PU membrane is produced by coating the resin on substrate and drying it to vaporize the solvent adequately. The membrane gives soft hand-feel and dry surface, and offers waterproof and windproof properties. Using one component type PU resin alone with adequate crosslinker for yarn fixation, following by drying process to vaporize solvent adequately, could form high yarn-bonding membrane. Shoes, leather bag, ready-make clothes Blocking resistance, high water resistance, good hand-feel High solid content PU resin for dry direct coating. Bright surface, non-sticky. Contain no toxic organic tin.

Message

One component PU Resins

PU membrane is produced by coating the resin on substrate and drying it to vaporize the solvent adequately. The membrane gives soft hand-feel and dry surface, and offers waterproof and windproof properties. Using one component type PU resin alone with adequate crosslinker for yarn fixation, following by drying process to vaporize solvent adequately, could form high yarn-bonding membrane.

Shoes, leather bag, ready-make clothes

Blocking resistance, high water resistance, good hand-feel

High solid content PU resin for dry direct coating. Bright surface, non-sticky. Contain no toxic organic tin.

General Information
Features	Crosslinkable Non-Stick
Uses	Adhesives Coating Applications Footwear
Appearance	Clear/Transparent Transparent - Slight Yellow

Additional Information	Nominal Value	Unit
Solvents	DMF/TOL

Uncured Properties	Nominal Value	Unit
Color	Clear/Transparent Colorless Clear, Light Yellow
Solids Content	59 to 61	%
Viscosity (25°C)	60 to 80	Pa·s

Cured Properties	Nominal Value	Unit
Tensile Modulus (100% Secant)	< 0.490	MPa
Tensile Strength	< 0.981	MPa
Tensile Elongation at Break	< 100	%

Resin Grade	Manufacturer	Category	Trademark
SEPAZ™ C130HS	Mando Advanced Materials Co., Ltd.	LCP	SEPAZ™
Starpylen M1000-BK1A987	Eurostar Engineering Plastics	PP, Unspecified	Starpylen
NAXELL™ PC110VL	MRC Polymers, Inc.	PC	NAXELL™
LNP™ THERMOCOMP™ MF002S compound	SABIC Innovative Plastics	PP, Unspecified	LNP™ THERMOCOMP™
Amodel® AE-8935	Solvay Specialty Polymers	PPA	Amodel®