DENILEN M 7039
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Vamp Tech |
| Trademark: | DENILEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IQQWHP_DENILEN-M-7039.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PP, 70% mineral filled, not Flame Retardant compound, good mechanical properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.99 | g/cm³ | ASTM D792 |
| Water Absorption (Saturation) | 0.020 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4000 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 20.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 5.0 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 4.0 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | 40 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 65.0 | °C | ASTM D648A |
| Vicat Softening Temperature | 95.0 | °C | ASTM D1525 1 |
| RTI Elec | 110 | °C | UL 746 |
| RTI Imp | 110 | °C | UL 746 |
| RTI Str | 110 | °C | UL 746 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 220 | °C | |
| Mold Temperature | 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Badamid® PA12 GM/GR40 H | Bada AG | Nylon 12 | Badamid® |
| Dialon 2530 | DTR S.r.l. (Develop Thermoplastic Resins) | PC | Dialon |
| DURANEX® HN7315N/B | Polyplastics Co., Ltd. | PC+PBT | DURANEX® |
| KMI PP KM-5161H | KMI Group, Inc. | PP Homopolymer | KMI PP |
| LG EVA EA19150 | LG Chem Ltd. | EVA | LG EVA |