SUPREME GPPS SC201LV

Category:	PS (GPPS) , General Purpose Polystyrene
Manufacturer:	Supreme Petrochem Ltd.
Trademark:	SUPREME GPPS
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	IQNsaE_SUPREME-GPPS-SC201LV.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

General Purpose Polystyrene

Characteristics:

High Molecular Weight Grade

Medium Heat, Good Toughness

Good Flow Properties along with Good Mechanical Strength

Easy processability with Good Mold Release Properties.

Processing:

Molding

Applications:

Suitable for large volume clear molded products.

Refrigerator componenets like crisper trays, egg shells etc.

tooth brush, tooth brush containers, lay flat boxes, ball pen barrels, geometrical appliances etc.

General Information
Additive	Mold Release
Features	Food Contact Acceptable Good Flow Good Mold Release Good Processability Good Strength Good Toughness High Molecular Weight Medium Heat Resistance
Uses	Appliances Containers Packaging Toothbrush Handles
Agency Ratings	FDA 21 CFR 177.1640
Appearance	Clear/Transparent
Forms	Pellets
Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.04	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (200°C/5.0 kg)	2.5	g/10 min	ASTM D1238

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength ¹(23°C, 3.20 mm, Injection Molded)	49.0	MPa	ASTM D638
Tensile Elongation ²(Break, 23°C, 3.20 mm, Injection Molded)	2.0	%	ASTM D638
Flexural Modulus (23°C, 3.20 mm, Injection Molded)	2700	MPa	ASTM D790
Flexural Strength (23°C, 3.20 mm, Injection Molded)	82.0	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C, 3.20 mm, Injection Molded)	20	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed, Injection Molded)	78.0	°C	ASTM D648
Vicat Softening Temperature	96.0	°C	ASTM D1525 ³

Flammability	Nominal Value		Test Method
Flame Rating (1.60 mm)	HB		UL 94

Injection	Nominal Value	Unit
Processing (Melt) Temp	180 to 260	°C
Mold Temperature	40.0 to 60.0	°C

Note Message
1 .	50 mm/min
2 .	50 mm/min
3 .	Rate B (120°C/h), Loading 1 (10 N)

Resin Grade	Manufacturer	Category	Trademark
ChronoThane™ T 93A-B40	AdvanSource Biomaterials Corp.	TPU-Polyether	ChronoThane™
Elastocon® 8068BL	Elastocon TPE Technologies	TPE	Elastocon®
KW Plastics KW 622	KW Plastics	PP Copolymer	KW Plastics
Karina GRAY PVC COMPOUND -E711D18/305-B-IS	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
ESTOPLAST EP 1500WW5DP	Ester Industries Ltd.	PBT	ESTOPLAST EP