NORYL™ WCD933 resin
| Category: | PPE+TPE , Polyphenylene Ether + TPE |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IQ2XMQ_NORYL-WCD933-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Flexible and non-halogenated flame retardant extrusion grade intended for evaluation in applications such as insulation of HD 21.14 flexible cables. Flame retardant performance capable of meeting EN 50265-2-1 requirement. 93 Shore A hardness. Processing typically conducted on standard extrusion equipment. Wire tests conducted on 2.0 mm wire with 0.12 mm x 20 stranded copper conductor. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/10.0 kg) | 8.5 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 30 sec) | 93 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Fracture | 15.0 | MPa | UL 1581 |
| Fracture 1 | 9.00 | MPa | ASTM D638 |
| Fracture, 80°C 2 | 15.0 | MPa | UL 1581 |
| Fracture | 9.00 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Fracture | 310 | % | UL 1581 |
| Fracture 3 | 130 | % | ASTM D638 |
| Fracture, 80°C 4 | 270 | % | UL 1581 |
| Fracture | 180 | % | ISO 527-2/50 |
| Flexural Modulus 5 | |||
| 100mm span | 160 | MPa | ASTM D790 |
| -- | 135 | MPa | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -40.0 | °C | ASTM D746 |
| Heat Deformation (100°C) 6 | 10 | % | UL 1581 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vertical Flame Test | PASSES | EN 50265-2-1 | |
| Smoke Density | ASTM E662 | ||
| Flame, 0.5 mm plaque, Ds, max | 56 | ASTM E662 | |
| Non-Flame, 0.5 mm plaque, Ds, max | 150 | ASTM E662 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm, in Oil) | 23 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 MHz) | 3.00 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 1.0E-3 | ASTM D150 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index (3.00 mm) | 750 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (3.00 mm) | 775 | °C | IEC 60695-2-13 |
| Oxygen Index | 29 | % | ISO 4589-2 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 - 85.0 | °C | |
| Drying Time | 5.0 - 7.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Cylinder Zone 1 Temp. | 180 - 220 | °C | |
| Cylinder Zone 3 Temp. | 220 - 250 | °C | |
| Cylinder Zone 5 Temp. | 220 - 250 | °C | |
| Melt Temperature | 220 - 250 | °C | |
| Die Temperature | 220 - 250 | °C |
| Extrusion instructions |
|---|
| Conductor Pre-heat Temperature: 25 - 120 °CCooling Water Air Gap: 100 - 200 mmCross-head Temperature: 220 - 250 °CDrying Time (Cumulative): 12 hrsExtruder Length/Diameter Ratio (L/D): 22:1 to 26:1Neck Temperature: 220 - 250 °CScreen Pack: 150 - 100Screw Speed: 15 - 85 rpmWater Bath Temperature: 15 - 60 °C |
| Note Message | |
|---|---|
| 1 . | Type 1, 50mm/min |
| 2 . | After 7 days |
| 3 . | Type 1, 50mm/min |
| 4 . | After 7 days |
| 5 . | 13 mm/min |
| 6 . | 250 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Softell CA 7413 A | LyondellBasell Industries | TPO (POE) | Softell |
| Zytel® LC6601 NC010 | DuPont Performance Polymers | Nylon 612 | Zytel® |
| Novalloy-B B1700, B1700F | Daicel Polymer Ltd. | ABS+PBT | Novalloy-B |
| OmniCarb™ PC08FR GF10 | OMNI Plastics, LLC | PC | OmniCarb™ |
| Sylvin 916VO-85 Black 297 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |