LNP™ LUBRICOMP™ OL003A compound
| Category: | PPS, Branched , Branched Polyphenylene Sulfide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IOyKc1_LNP-LUBRICOMP-OL003A-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP OL003A is a compound based on PPS - Branched resin containing 15% PTFE. Added features of this grade are: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound OL-4030 Product reorder name: OL003A |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.44 | g/cm³ | |
| -- | 1.43 | g/cm³ | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.90 to 2.0 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.020 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.040 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3590 | MPa | ASTM D638 |
| -- | 3370 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 21.0 | MPa | ASTM D638 |
| Break | 20.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 0.60 | % | ASTM D638 |
| Break | 0.60 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 3870 | MPa | ASTM D790 |
| -- 5 | 3320 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 56.0 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 65.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 14 | J/m | ASTM D256 |
| 23°C 7 | 2.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 74 | J/m | ASTM D4812 |
| 23°C 8 | 4.8 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 1.00 | J | ASTM D3763 |
| -- | 0.400 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 175 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 178 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 108 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 109 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 6.0E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 6.6E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 304 to 316 | °C | |
| Middle Temperature | 321 to 332 | °C | |
| Front Temperature | 332 to 343 | °C | |
| Processing (Melt) Temp | 316 to 321 | °C | |
| Mold Temperature | 138 to 166 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrathane™ ARC-72D-B20 | Biomerics, LLC | TPU-PC | Quadrathane™ |
| Spartech Polycom E65050 | Spartech Polycom | PVC, Unspecified | Spartech |
| Sypex M1620GN | Ginar Technology Co., LTD. | ABS | Sypex |
| Moplen HP401R | LyondellBasell Industries | PP Homopolymer | Moplen |
| Colorite 11 Series 9811 | Colorite Polymers | PVC, Unspecified | Colorite 11 Series |