Innothane® IE-3076
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | Innothane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IOeFGM_Innothane-IE-3076.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| IE-3076 is an 80 shore D polyurethane formulated for room temperature hand-batch processing. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury, MOCA or TDI. IE-3076 is particularly ideal for color-matching applications due to its neutral, semi-transparent appearance. |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Cured | 1.11 | g/cm³ | |
| Hardener | 1.11 | g/cm³ | |
| Matrix resin | 1.25 | g/cm³ | |
| Molding Shrinkage - Flow | 0.20 - 0.40 | % | ASTM D2566 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 2690 | MPa | ASTM D790 |
| Flexural Strength | 114 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 37 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 83.0 | °C | ASTM D648 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Resin | Mixing ratio by capacity: 100 Mixing ratio by weight: 100 | ||
| Hardening method | Mixing ratio by capacity: 100 Mixing ratio by weight: 89 | ||
| Demold Time | 60 - 180 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 25°C 1 | 0.075 | Pa·s | |
| 25°C 2 | 0.30 | Pa·s | |
| 25°C 3 | 0.85 | Pa·s | |
| Curing Time 4 | 40 | hr | |
| Gel Time | 10 - 15 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 75 - 85 | ASTM D2240 | |
| Tensile Strength | 68.9 | MPa | ASTM D638 |
| Tensile Elongation at Break | 9.0 | % | ASTM D638 |
| Note Message | |
|---|---|
| 1 . | Resin |
| 2 . | Mixed |
| 3 . | Hardener |
| 4 . | 24 hours at 77°F + 16 hours at 200°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VICOTE® 706 | Victrex plc | PEEK | VICOTE® |
| Network Polymers PP PPB 25 2010 | Network Polymers, Inc. | PP Copolymer | Network Polymers PP |
| ELASTOSIL® M 4500 | Wacker Chemie AG | Silicone | ELASTOSIL® M |
| OmniLon™ PA6/6 U IM20 HS BK1000 | OMNI Plastics, LLC | Nylon 66 | OmniLon™ |
| Sylvin 9703-66 Yellow 4167 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |