TAIRIREX HP9450
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Formosa Plastics Corporation |
| Trademark: | TAIRIREX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IOcVIz_TAIRIREX-HP9450.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FCFC PS resin HP9450 meets the requirements of UL, RoHS, FDA and the certificates of environmental protection. |
| General Information | |
|---|---|
| Agency Ratings |
|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.04 | g/cm³ | ASTM D792 |
| 23°C | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 3.0 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| 23°C | 24.5 | MPa | ASTM D638 |
| 23°C | 25.0 | MPa | ISO 527-2 |
| Tensile Elongation (Break, 23°C) | 43 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus (23°C) | 2160 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | |||
| 23°C | 43.1 | MPa | ASTM D790 |
| 23°C | 43.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (23°C, 6.35 mm) | 140 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 1(1.8 MPa, Annealed, 3.18 mm) | 91.0 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | 97.0 | °C | ASTM D1525, ISO 306/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, Natural Color) | HB | UL 94 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Residual Monomer | < 700 | ppm |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 | °C | |
| Drying Time | 1.0 to 2.0 | hr | |
| Hopper Temperature | 40.0 | °C | |
| Rear Temperature | 200 | °C | |
| Middle Temperature | 220 | °C | |
| Front Temperature | 210 | °C | |
| Nozzle Temperature | 200 | °C | |
| Processing (Melt) Temp | 190 to 230 | °C | |
| Mold Temperature | 20.0 to 70.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 80°Cx2Hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2099 X 126210 BLACK | RTP Company | PLA+PC | RTP |
| Sumitomo DAP FS-5 | Sumitomo Bakelite North America, Inc. | DAP | Sumitomo DAP |
| DENKA EVA TEX 75 | Denka Company Limited | EVA | DENKA EVA TEX |
| Hanwha Total PP BJ550 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP Impact Copolymer | Hanwha Total PP |
| Karina CLEAR PVC COMPOUND -E 75/218-D-IS-AS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |