POLYfill PPH T5040DS
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Polykemi AB |
| Trademark: | POLYfill |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IOKVDo_POLYfill-PPH-T5040DS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Mineral reinforced Detergent resistant |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.80 to 1.0 | % | |
| Flow | 0.80 to 1.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 30.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 4.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 3800 | MPa | ISO 178 |
| Flexural Stress | 58.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 2.0 | kJ/m² | |
| 23°C | 3.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1 | |||
| 0.45 MPa, Unannealed | 125 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 75.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 148 | °C | ISO 306/A50 |
| -- | 88.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 750 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPREME PP SPEXP56 | Supreme Petrochem Ltd. | PP, Unspecified | SUPREME PP |
| Zhongfa PET G30FR | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PET | Zhongfa |
| COPEC® CC6OCZ (Series: VS/AD1) | KRAIBURG TPE | TPE | COPEC® |
| Formolene® HB5502S1 | Formosa Plastics Corporation, U.S.A. | HDPE | Formolene® |
| LUVOCOM® 1-7139-1 | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |