Ecomass® 4702ZB92
| Category: | TPU, Unspecified , Thermoplastic Polyurethane Elastomer |
| Manufacturer: | Ecomass Technologies |
| Trademark: | Ecomass® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IMDFlM_Ecomass-4702ZB92.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ecomass® 4702ZB92 is a Thermoplastic Polyurethane Elastomer material filled with filler. It is available in North America for injection molding. Important attributes of Ecomass® 4702ZB92 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 6.88 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 to 0.50 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 669 | MPa | ASTM D638 |
| Tensile Strength | 11.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 15 | % | ASTM D638 |
| Flexural Modulus | 448 | MPa | ASTM D790 |
| Flexural Strength | 20.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 160 | J/m | ASTM D256 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 to 93.3 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 204 to 221 | °C | |
| Mold Temperature | 10.0 to 26.7 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecomid® NB40 GR30 NL IM | Eurotec Engineering Plastics | Nylon 6 | Tecomid® |
| Arnite® TV4 261 /G -UN.02.09 | DSM Engineering Plastics | PBT | Arnite® |
| Chemlon® MDFS2 | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| Desmopan® DP 3360A DPS 061 | Covestro - PUR | TPU-Polyester | Desmopan® |
| Karina GRAY PVC COMPOUND 105900-18/121-B-ACE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |