Thermoplastic Polyester Polyurethane Elastomers with excellent mechanical properties. Outstanding tensile strength and high elongation at break, good damping characteristics, a high resilience performance and very good wear resistance. Typical applications Spiral tubing, pneumatic tubing, round belting, technical mouldings e.g. bushes, dust caps, seals, joints, blow moulded bellows, fan belts. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ISO 1183/A |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 3 sec) | 60 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 330 | MPa | ISO 527-2 |
| Abrasion Loss | 20.0 | mm³ | ISO 4649-A |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | DIN 53504 | ||
| 20% Strain | 16.0 | MPa | |
| 100% Strain | 20.0 | MPa | |
| 300% Strain | 35.0 | MPa | |
| Tensile Stress | DIN 53504 | ||
| Yield 1 | 43.0 | MPa | |
| Yield | 50.0 | MPa | |
| Tensile Elongation 2(Break) | 450 | % | DIN 53504 |
| Tear Strength 3 | 180 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| 23°C, 72 hr | 40 | % | |
| 70°C, 24 hr | 50 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 8.0 | kJ/m² | |
| 23°C | No Break |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 170 to 240 | °C | |
| Mold Temperature | 20.0 to 70.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 150 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | after storage in water for 21 days at 80°C |
| 2 . | after storage in water for 21 days at 80°C |
| 3 . | Method Bb, Angle (Nicked) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYMAN® (ABS) LP 137 A | A. Schulman Europe | ABS | POLYMAN® |
| NuSil MED3-4213 | NuSil Technology | Silicone | NuSil |
| Hostacom CR 1171 G1 C12541 | LyondellBasell Industries | PP Copolymer | Hostacom |
| LNP™ THERMOCOMP™ DX06411 compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |
| LNP™ STAT-KON™ DE006ER compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |