Mowital® B 45 M
| Category: | PVB , Polyvinyl Butyral |
| Manufacturer: | Kuraray Co., Ltd. |
| Trademark: | Mowital® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IKOwHM_Mowital-B-45-M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Characteristics Polyvinyl butyral (PVB) grades with different molecular weights, and varying degrees of acetalization. Recommended Uses Binder for coatings (adhesion promotion/corrosion protection primers, shop primers, wash primers, stoving enamels, varnishes and lacquers for different substrates). Binder for printing inks. Co-binder for powder coatings. Temporary binder for ceramics. Binder for textile printing and non-woven. Wetting agent for grindings, esp. of organic pigments. Adhesives, pressure-sensitive adhesives and hotmelts. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Density | 0.25 | g/cm³ | DIN EN 543 |
| Water Absorption (20°C, 24 hr, 0.100 mm) | 5.0 to 8.0 | % | |
| Solution Viscosity 1 | 80 to 110 | mPa·s | DIN 53015 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 70.0 | °C | ISO 11357-2 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Non-Volatile Content | > 97.5 | wt% | DIN 53216 |
| Polyvinyl Acetate Content 2 | 1.0 to 4.0 | wt% | |
| Polyvinyl Alcohol Content 3 | 21.0 to 24.0 | wt% |
| Note Message | |
|---|---|
| 1 . | According to Hoeppler, 10% solution in Ethanol containing 5% water at 20°C |
| 2 . | Acetyl groups in terms of polyvinyl acetate |
| 3 . | Hydroxyl groups in terms of polyvinyl alcohol |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ResMart Plus ABS Black | ResMart | ABS | ResMart Plus |
| Moldex® QS251D/QCM240 | Mitsubishi Chemical Corporation | Polyolefin, Unspecified | Moldex® |
| Fainplast PVC PMS 60 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Geon™ HTX LA550 | PolyOne Corporation | PVC Alloy | Geon™ HTX |
| Karina GRAY PVC COMPOUND 702-DA-18/406-BZ-AS (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |