Ultramid® 8270 HS BK-102
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IIspQO_Ultramid-8270-HS-BK-102.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid 8270 HS BK-102 is a thermally modified pigmented black, PA6 blow molding compound exhibiting exceptional toughness and melt strength ideally suited for blow molding, profile extrusion, and other applications requiring extra high melt viscosity. It exhibits excellent permeability and chemical resistance to oils, hydrocarbons and most solvents. Applications Ultramid 8270 HS BK-102 is generally recommended for applications such as industrial containers, small gasoline tanks, and automotive under hood reservoirs. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.13 | -- | g/cm³ | ASTM D792 |
| Water Absorption | ASTM D570 | |||
| 24 hr | 1.6 | -- | % | |
| Saturation | 9.2 | -- | % | |
| Equilibrium, 50% RH | 2.6 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 99 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | ASTM D638 | |||
| Yield, -40°C | 138 | 119 | MPa | |
| Yield, 23°C | 84.0 | 46.0 | MPa | |
| Yield, 121°C | 24.0 | -- | MPa | |
| Tensile Elongation | ASTM D638 | |||
| Yield, 23°C | 4.0 | -- | % | |
| Break, 23°C | > 100 | -- | % | |
| Flexural Modulus | ASTM D790 | |||
| -40°C | 3160 | 3900 | MPa | |
| 23°C | 2900 | 760 | MPa | |
| 65°C | 435 | -- | MPa | |
| 90°C | 310 | -- | MPa | |
| 121°C | 260 | -- | MPa | |
| Flexural Strength | ASTM D790 | |||
| -40°C | 179 | 176 | MPa | |
| 23°C | 114 | 37.0 | MPa | |
| 65°C | 30.0 | -- | MPa | |
| 90°C | 20.0 | -- | MPa | |
| 121°C | 17.0 | -- | MPa |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | ASTM D256 | |||
| -40°C | 53 | 48 | J/m | |
| 23°C | 53 J/m | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | 169 | -- | °C | |
| 1.8 MPa, Unannealed | 63.0 | -- | °C | |
| Peak Melting Temperature | 220 | -- | °C | ASTM D3418 |
| CLTE - Flow | 1.4E-4 | -- | cm/cm/°C | ASTM E831 |
| Additional Information | Dry | Conditioned | Unit | |
|---|---|---|---|---|
| Blow Molding Drying Temperature | 80 | -- | °C | |
| Blow Molding Drying Time | 2.0 to 4.0 | -- | hr | |
| Blow Molding Melt Temperature | 245 to 260 | -- | °C | |
| Blow Molding Moisture Content | < 0.15 | -- | % | |
| Blow Molding Mold Temperature | 60 | -- | °C | |
| Blow-up Ratio | 2:1 | -- |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 5132-86 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Vydyne® R550H NT662 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| Ceramer 20 | Ceramer GmbH | PPSU | Ceramer |
| MAJORIS AT231 - 8229 | AD majoris | PP, Unspecified | MAJORIS |
| Delene 2030 | Shanghai Lin Gen Rubber Materials Co., Ltd. | TPE | Delene |