DOW™ LDPE 303E
| Category: | LDPE , Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IIq5Rq_DOW-LDPE-303E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOW LDPE 303E Low Density Polyethylene Resin contains no slip or antiblock additives. DOW LDPE 303E Low Density Polyethylene Resin can readily be extruded using the blown film techniques utilising melt temperatures between 160 and 200 ° C. Main Characteristics:
Applications:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.922 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.30 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 200 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 200 µm | 10.0 | MPa | ASTM D882 |
| TD : Yield, 200 µm | 11.0 | MPa | ASTM D882 |
| MD : Break, 200 µm | 23.0 | MPa | ASTM D882 |
| TD : Break, 200 µm | 24.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 200 µm | 580 | % | ASTM D882 |
| TD : Break, 200 µm | 720 | % | ASTM D882 |
| Dart Drop Impact (200 µm) | 700 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 200 µm | 900 | g | ASTM D1922 |
| TD : 200 µm | 1400 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 98.0 | °C | ASTM D1525 |
| Extrusion instructions |
|---|
| 放大比 1:2.5 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVALEN® PH 22 T 40 | Plastcom | PP, Unspecified | SLOVALEN® |
| TOTAL Polystyrene Impact 830 | TOTAL Refining & Chemicals | PS (HIPS) | TOTAL Polystyrene |
| Badamid® A70 GF30 H | Bada AG | Nylon 66 | Badamid® |
| Expandable PS F42B | INEOS Styrenics International SA | PS (EPS) | Expandable PS |
| POLIMAXX 2563LCXTA5 | IRPC Public Company Limited | PP Impact Copolymer | POLIMAXX |