LNP™ COLORCOMP™ M1000S compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ COLORCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IFigSX_LNP-COLORCOMP-M1000S-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP COLORCOMP* M1000S is an unfilled Polypropylene resin. Added features of this material include: Heat Stabilized. Also known as: LNP* COLORCOMP* Compound M-1000 HS Product reorder name: M1000S |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.13 | g/cm³ | ASTM D792 |
| -- | 1.12 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow : 24 hr | 1.5 to 1.7 | % | |
| Across Flow : 24 hr | 1.5 to 1.7 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2160 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 28.0 | MPa | |
| Break | 26.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 7.0 | % | |
| Break | 40 | % | |
| Flexural Modulus | 1800 | MPa | ISO 178 |
| Flexural Stress | 40.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 1(23°C) | 3.5 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 2 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 130 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 94.0 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 193 to 204 | °C | |
| Middle Temperature | 199 to 210 | °C | |
| Front Temperature | 204 to 216 | °C | |
| Processing (Melt) Temp | 216 to 221 | °C | |
| Mold Temperature | 32.2 to 48.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 80*10*4 |
| 2 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SRF3834 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| TRAMID® 4110G40 | Samyang Corporation | Nylon, Unspecified | TRAMID® |
| AIE PBT 30G6F | Asia International Enterprise (Hong Kong) Limited | PBT | AIE PBT |
| KumhoSunny ABS HAG5220FR | Shanghai KumhoSunny Plastics Co., Ltd. | ABS | KumhoSunny ABS |
| SQUARE® LIM3600-30A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |