| Staramide RF00ASXS is a 50 % Glass Fiber Reinforced Polyamide 66 Injection Molding Resin |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.57 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (4.00 mm) | 0.10 to 0.30 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.70 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 15400 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 210 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.4 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 14100 | MPa | ISO 178 |
| Flexural Stress | 305 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 15 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 80 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 259 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 246 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 2.6E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 8.4E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 85.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 to 280 | °C | |
| Middle Temperature | 270 to 280 | °C | |
| Front Temperature | 270 to 290 | °C | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RALUPOL® UP 4806 | RASCHIG GmbH | Polyester, TS | RALUPOL® |
| SUPRENE® 512F | SK Global Chemical | EPDM | SUPRENE® |
| Kepamid® 2300SF | Korea Engineering Plastics Co., Ltd | Nylon 66 | Kepamid® |
| LNP™ LUBRICOMP™ RFL26S compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |
| Moplen EP300C | PolyMirae | PP Impact Copolymer | Moplen |