DESLOY™ DSC892D
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | DESCO Co., Ltd. |
| Trademark: | DESLOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IBGHpf_DESLOY-DSC892D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Descriptions: DESLOY™ DSC892D is PC & ABS alloy resin which has an advantage of both resins. It has good rigidity and toughness. DESLOY™ DSC892D also has low water absorption and excellent dimensional stability. Applications: DESLOY™ DSC892D is applied to automotive lamp housing which request good mechanical property ,non-glossy and low deformation property. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.50 - 0.70 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 63.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 120 | % | ASTM D638 |
| Flexural Modulus | 2450 | MPa | ASTM D790 |
| Flexural Strength | 88.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 540 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 110 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 85.0 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 120 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Suggested Max Moisture | < 0.20 | % | |
| Rear Temperature | 250 - 260 | °C | |
| Middle Temperature | 260 - 270 | °C | |
| Front Temperature | 260 - 280 | °C | |
| Nozzle Temperature | 260 - 280 | °C | |
| Processing (Melt) Temp | 260 - 280 | °C | |
| Mold Temperature | 60.0 - 90.0 | °C |
| Injection instructions |
|---|
| Speed: 40 to 70%Pressure 1st: 30 to 60%Pressure 2nd: 30 to 60Holding Pressure: 10 to 20% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TUFNYL® RGF 34 NATURAL | SRF Ltd. | Nylon 66 | TUFNYL® |
| Ultramid® B36 LN 01 | BASF Corporation | Nylon 6 | Ultramid® |
| 3M™ Dyneon™ TFM™ Modified PTFE TFM 2033Z | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE |
| Gallonprene® GP520-9009 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| LEXAN™ EXL1890T resin | SABIC Innovative Plastics | PC | LEXAN™ |