LNP™ LUBRICOMP™ RFL33 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IA5t9q_LNPLUBRICOMPRFL33compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP RFL33 is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound RFL-4033 Product reorder name: RFL33 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.37 | g/cm³ | ASTM D792 |
| -- | 1.36 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.50 - 0.70 | % | ASTM D955 |
| Transverse flow : 24 hours | 1.6 - 1.8 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 1.7 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.64 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.60 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6890 | MPa | ASTM D638 |
| -- | 6440 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 120 | MPa | ASTM D638 |
| Yield | 118 | MPa | ISO 527-2 |
| Fracture | 120 | MPa | ASTM D638 |
| Fracture | 118 | MPa | ISO 527-2 |
| Tensile Elongation | ASTM D638, ISO 527-2 | ||
| Yield | 3.1 | % | ASTM D638, ISO 527-2 |
| Fracture | 3.1 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 5520 | MPa | ASTM D790 |
| -- | 5800 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 179 | MPa | ASTM D790 |
| -- | 183 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.40 | ASTM D3702 Modified | |
| With Self-Static | 0.45 | ASTM D3702 Modified | |
| Wear Factor - Washer | 19.5 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 64 | J/m | ASTM D256 |
| 23°C 2 | 6.7 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 570 | J/m | ASTM D4812 |
| 23°C 3 | 35 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 7.60 | J | ASTM D3763 |
| -- | 2.10 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 261 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 260 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 247 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 243 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 8.3E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 4.0E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 3.9E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 - 0.25 | % | |
| Rear Temperature | 266 - 277 | °C | |
| Middle Temperature | 282 - 293 | °C | |
| Front Temperature | 293 - 304 | °C | |
| Processing (Melt) Temp | 282 - 304 | °C | |
| Mold Temperature | 93.3 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205 TFE 10 FR | RTP Company | Nylon 66 | RTP |
| ALTECH® PA66 A 2015/710 GF15 IM | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |
| APEX® 04-A0386B-88 | Teknor Apex Company | PVC, Flexible | APEX® |
| AURAPENE PPUFBKIMP | Aurora Manufacturing Ltd | TPO | AURAPENE |
| Wuxi Jiahong EB-202 | Wuxi Jiahong Plastics Technology CO., Ltd. | PVC, Unspecified | Wuxi Jiahong |