EMERGE™ PC 4202-8
| Category: | PC , Advanced Resin |
| Manufacturer: | Trinseo |
| Trademark: | EMERGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | I9tgDE_EMERGE-PC-4202-8.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EMERGE™ PC 4202 advanced resin is 20% glass reinforced polycarbonate containing mold release for optimal processing. This resin exhibits high modulus and excellent dimensional stability. It is available in 8 and 15 Melt Flow Rates. EMERGE PC 4202 resin is typically used in injection molding applications. Applications are information technology equipment, electrical parts, other structural/internal parts. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.36 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.20 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 122 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5170 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 82.7 | MPa | |
| Break | 82.7 | MPa | |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 4960 | MPa | ASTM D790 |
| Flexural Strength | 148 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Annealed | 148 | °C | |
| 1.8 MPa, Unannealed | 138 | °C | |
| 1.8 MPa, Annealed | 142 | °C | |
| Vicat Softening Temperature | 159 | °C | ASTM D1525 1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 2 | UL 94 | ||
| 1.60 mm | V-2 | ||
| 3.05 mm | V-0 | ||
| Oxygen Index 3 | 30 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Melt Temperature (Aim) | 288 | °C | |
| Mold Temperature | 82.2 | °C |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| 2 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 3 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer KEG-2000-50A/B | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| WPP PP PPH3GF3-Natural | Washington Penn Plastic Co. Inc. | PP Homopolymer | WPP PP |
| PERCOM® XG1128/2 | A. Schulman Europe | PP, Unspecified | PERCOM® |
| OTECH PVC OE9028 - Profile | OTECH Corporation | PVC, Unspecified | OTECH PVC |
| Sylvin 9067-82C White 1205 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |