Medalist® MD-50138D
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Medalist® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | I89r16_Medalist-MD-50138D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Medalist™MD-50138D is a thermoplastic elastomer (TPE) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is extrusion or injection molding. Typical application areas include:
|
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.888 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw D, 1 sec | 40 | ASTM D2240 | |
| Shaw D, 5 seconds | 38 | ASTM D2240 | |
| Shaw D, 10 seconds | 35 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 172 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 17.9 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 580 | % | ASTM D412 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 127 - 149 | °C | |
| Middle Temperature | 138 - 160 | °C | |
| Front Temperature | 149 - 171 | °C | |
| Nozzle Temperature | 171 - 193 | °C | |
| Processing (Melt) Temp | 171 - 193 | °C | |
| Mold Temperature | 21.1 - 37.8 | °C | |
| Injection Pressure | 1.38 - 5.52 | MPa | |
| Back Pressure | 0.172 - 0.689 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| Drying is not necessary. However, if moisture is a problem, dry the pellets for 2 to 4 hours at 150°F (65°C). |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 171 - 188 | °C | |
| Cylinder Zone 2 Temp. | 182 - 196 | °C | |
| Cylinder Zone 3 Temp. | 185 - 204 | °C | |
| Cylinder Zone 5 Temp. | 204 - 227 | °C | |
| Die Temperature | 204 - 227 | °C |
| Extrusion instructions |
|---|
| Screw Speed: 30 to 100 rpm.Screen Pack Recommendation:60/200/200/60 to 60/200/400/400/200/60 mesh size. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx P63E0 | The Matrixx Group, Inc. | Nylon 6 | Matrixx |
| Evoprene™ GC 5617 | AlphaGary | SEBS | Evoprene™ GC |
| Hostacom M4 U05 102943 | LyondellBasell Industries | PP Homopolymer | Hostacom |
| Karina BLACK PVC COMPOUND CAK 65-48/ 1-F (GERDAU) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LEXAN™ OQ4320R resin | SABIC Innovative Plastics | PC | LEXAN™ |