Tritan™ LX500
| Category: | Copolyester , Thermoplastic Polyester |
| Manufacturer: | Eastman Chemical Company |
| Trademark: | Tritan™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | I7tnyN_Tritan-LX500.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Eastman Tritan™ LX500 is an amorphous copolyester specifically developed for use in blow molding applications for the cosmetic, fragrance, and personal care markets. Its most outstanding features are excellent toughness, hydrolytic stability, and heat and chemical resistance. In addition, this new generation copolyester offers excellent appearance and clarity. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- | 1610 | MPa | ASTM D638 |
| -- | 1570 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield | 44.8 | MPa | ASTM D638 |
| Yield | 45.0 | MPa | ISO 527-2 |
| Fracture | 52.4 | MPa | ASTM D638 |
| Fracture | 51.0 | MPa | ISO 527-2 |
| Tensile Elongation | ASTM D638, ISO 527-2 | ||
| Yield | 7.0 | % | ASTM D638, ISO 527-2 |
| Fracture | 140 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 1520 | MPa | ASTM D790 |
| -- | 1490 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 60.0 | MPa | ISO 178 |
| Yield | 64.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 840 | J/m | ASTM D256 |
| -40°C | 12 | kJ/m² | ISO 180 |
| 23°C | 78 | kJ/m² | ISO 180 |
| Unnotched Izod Impact (23°C) | No Break | ASTM D4812 | |
| Instrumented Dart Impact | ASTM D3763 | ||
| -40°C | 67.0 | J | ASTM D3763 |
| 0°C | 65.0 | J | ASTM D3763 |
| 23°C | 62.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 101 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 85.0 | °C | ISO 75-2/A |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (Total) | 91.0 | % | ASTM D1003 |
| Haze | < 1.0 | % | ASTM D1003 |
| Additional Information |
|---|
| EBM Processing Melt Temperature: 235 to 255°CEBM Blow Mold Temperature: 15 to 50°CISBM Processing Melt Temperature: 260 to 280°CISBM Injection Mold Temperature: 40 to 65°CISBM Blow Mold Temperature: 35 to 55°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 88.0 | °C | |
| Drying Time | 4.0 - 6.0 | hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® PVC PIPE GRADE | Marco Polo International, Inc. | PVC, Rigid | MARPOL® PVC |
| RTP 3400 G-540 | RTP Company | LCP | RTP |
| SCLAIR® 2815 | NOVA Chemicals | HDPE | SCLAIR® |
| Nypol® PA B3 G50 NTLA010 NT322 | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| Elastron® G G301.A65.B | Elastron USA, Inc. | SEBS | Elastron® G |