Stanyl® HGR2 BK00001
| Category: | Nylon 46 , Polyamide 46 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Stanyl® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | I7GLqB_StanylHGR2BK00001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Stanyl®HGR2 BK00001 is a polyamide 46 (nylon 46) material,. This product is available in North America, Europe or Asia Pacific,. Stanyl®The main features of HGR2 BK00001 are:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.26 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow | 2.0 | -- | % | ISO 294-4 |
| Flow | 2.0 | -- | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 3.2 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ISO 527-2 | |||
| -- | 3100 | 900 | MPa | ISO 527-2 |
| 120°C | 775 | -- | MPa | ISO 527-2 |
| 160°C | 650 | -- | MPa | ISO 527-2 |
| 180°C | 600 | -- | MPa | ISO 527-2 |
| 200°C | 560 | -- | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | |||
| Yield, 120°C | 45.0 | -- | MPa | ISO 527-2 |
| Yield, 160°C | 40.0 | -- | MPa | ISO 527-2 |
| Yield, 180°C | 35.0 | -- | MPa | ISO 527-2 |
| Yield, 200°C | 300 | -- | MPa | ISO 527-2 |
| Fracture | 90.0 | 60.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 20 | > 50 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | ISO 527-2 | |||
| 120°C | > 50 | -- | % | ISO 527-2 |
| 160°C | > 50 | -- | % | ISO 527-2 |
| 180°C | > 50 | -- | % | ISO 527-2 |
| 200°C | > 50 | -- | % | ISO 527-2 |
| Flexural Modulus | 2600 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | -- | ISO 179/1eU | |
| Notched Izod Impact (23°C) | 8.5 | -- | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 290 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 190 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 295 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow | 8.5E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.1E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Thermal Index - 5000 hrs | 152 | -- | °C | IEC 60216 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 80 - 110 | °C | |
| Rear Temperature | 290 - 315 | °C | |
| Middle Temperature | 295 - 315 | °C | |
| Front Temperature | 300 - 315 | °C | |
| Nozzle Temperature | 295 - 315 | °C | |
| Processing (Melt) Temp | 300 - 315 | °C | |
| Mold Temperature | 80 - 120 | °C | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 1.00 - 5.00 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 100 GB 20 HI | RTP Company | PP Copolymer | RTP |
| Monprene® RG-20160 X (PRELIMINARY DATA) | Teknor Apex Company | TPE | Monprene® |
| Elastocon® OF70B | Elastocon TPE Technologies | TPE | Elastocon® |
| Plaslube® J-1/CF/10/TF/20 BK | Techmer Engineered Solutions | Nylon 66 | Plaslube® |
| Kepamid® 1900SE | Korea Engineering Plastics Co., Ltd | Nylon 6 | Kepamid® |