Formolene® 2610A
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Formosa Plastics Corporation, U.S.A. |
| Trademark: | Formolene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | I6WSMv_Formolene-2610A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Formolene® 2610A is a high impact copolymer of polypropylene designed for such applications as Automotive Compounds and injection molding of Lawn & Garden products and Appliances. It is characterized by its easy mold flow, excellent physical property balance of stiffness and impact at room temperature and sub ambient conditions as well as finished product dimensional stability. Formolene® 2610A complies with the U. S. Food and Drug Administration regulation 21 CFR 177.1520(c)(3.4). This material may only be used in contact with foods of type I, II, III, IV-B, VI, VII, VIII and IX as described in Table 1 of 21 CFR 176.170(c) |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, Injection Molded) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, Injection Molded) | 20.3 | MPa | ASTM D638 |
| Tensile Elongation 2(Yield, Injection Molded) | 6.0 | % | ASTM D638 |
| Flexural Modulus - 1% Secant 3(Injection Molded) | 965 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, Injection Molded | 91 | J/m | |
| -18°C, Injection Molded | 100 | J/m | |
| 23°C, Injection Molded | 590 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, Injection Molded | 85.0 | °C | |
| 1.8 MPa, Unannealed, Injection Molded | 50.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P1785 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Moplen EP310D | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| Xuchuan XCW-8850N-12 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Eastar™ MN059 Natural | Eastman Chemical Company | Copolyester | Eastar™ |
| Karina IVORY PVC COMPOUND 650-35/1-A-EX | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |