LNP™ THERMOCOMP™ LX04015 compound
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | I5Gmv9_LNP-THERMOCOMP-LX04015-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP LX04015 is a compound based on Polyetheretherketone containing Carbon Fiber. Added features include: Electrically Conductive Also known as: LNP* THERMOCOMP* Compound PDXL04015 Product reorder name: LX04015 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.34 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.10 to 0.30 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 13800 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 200 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 11100 | MPa | ISO 178 |
| Flexural Stress | 275 | MPa | ISO 178 |
| Flexural Strain at Break 2 | 3.1 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 3(23°C) | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(23°C) | 30 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5(1.8 MPa, Unannealed, 64.0 mm Span) | 300 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 1.0E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 5.4E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+4 to 1.0E+7 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 349 to 360 | °C | |
| Middle Temperature | 366 to 377 | °C | |
| Front Temperature | 382 to 393 | °C | |
| Processing (Melt) Temp | 382 to 388 | °C | |
| Mold Temperature | 138 to 166 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Bamtac BPP245B | Ningbo Bamtac New Material Col, Ltd. | PP, Unspecified | Bamtac |
| ECOMID ARX H GF40 | Nilit Plastics | Nylon 66 | ECOMID |
| HANWHA CP-430 | Hanwha Chemical | PVC Copolymer | HANWHA |
| Kumho SBR 1712C | Korea Kumho Petrochemical Co., Ltd. | SBR, Emulsion | Kumho SBR |
| Sarlink® TPE ME-2375B (PRELIMINARY DATA) | Teknor Apex Company | TPE | Sarlink® TPE |