Makrolon® 3108
| Category: | PC , Polycarbonate |
| Manufacturer: | Covestro - Polycarbonates |
| Trademark: | Makrolon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | I5EZe5_Makrolon-3108.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| MVR (300 °C/1.2 kg) 6.0 cm³/10 min; medical devices; suitable for ETO and steam sterilization at 121 °C; biocompatible according to many ISO 10993-1 test requirements; high viscosity; injection molding - melt temperature 280 - 320 °C; available in transparent and opaque colors |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.20 | g/cm³ | ISO 1183 |
| Apparent Density 1 | 0.66 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 6.5 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 6.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Across Flow | 0.60 to 0.80 | % | ISO 2577 |
| Flow | 0.60 to 0.80 | % | ISO 2577 |
| Across Flow : 2.00 mm 2 | 0.75 | % | ISO 294-4 |
| Flow : 2.00 mm 3 | 0.70 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.30 | % | |
| Equilibrium, 23°C, 50% RH | 0.12 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 111 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2350 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 23°C | 65.0 | MPa | |
| Break, 23°C | 75.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 23°C | 6.3 | % | |
| Break, 23°C | 120 | % | |
| Nominal Tensile Strain at Break (23°C) | > 50 | % | ISO 527-2/50 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 2200 | MPa | |
| 1000 hr | 1900 | MPa | |
| Flexural Modulus 4(23°C) | 2350 | MPa | ISO 178 |
| Flexural Stress 5 | ISO 178 | ||
| 3.5% Strain, 23°C | 72.0 | MPa | |
| 23°C | 96.0 | MPa | |
| Flexural Strain at Flexural Strength 6(23°C) | 7.2 | % | ISO 178 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flash Ignition Temperature | 480 | °C | ASTM D1929 |
| Self Ignition Temperature | 550 | °C | ASTM D1929 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| ISO Shortname | ISO 7391-PC,M,(,,)-09-9 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 7 | ISO 7391 | ||
| -30°C, Complete Break | 18 | kJ/m² | |
| 23°C, Partial Break | 80 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -60°C | No Break | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength 8 | ISO 180/A | ||
| -30°C, Complete Break | 16 | kJ/m² | |
| 23°C, Partial Break | 90 | kJ/m² | |
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | ||
| -30°C | 70.0 | J | |
| 23°C | 60.0 | J | |
| Multi-Axial Instrumented Impact Peak Force | ISO 6603-2 | ||
| -30°C | 6500 | N | |
| 23°C | 5600 | N |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 141 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 129 | °C | ISO 75-2/A |
| Glass Transition Temperature 9 | 149 | °C | ISO 11357-2 |
| Vicat Softening Temperature | |||
| -- | 149 | °C | ISO 306/B50 |
| -- | 150 | °C | ISO 306/B120 |
| Ball Pressure Test (140°C) | Pass | IEC 60695-10-2 | |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 55°C | 6.5E-5 | cm/cm/°C | |
| Transverse : 23 to 55°C | 6.5E-5 | cm/cm/°C | |
| Thermal Conductivity 10(23°C) | 0.20 | W/m/K | ISO 8302 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index 11 | 1.587 | ISO 489 | |
| Transmittance | ISO 13468-2 | ||
| 1000 µm | 89.0 | % | |
| 2000 µm | 89.0 | % | |
| 3000 µm | 88.0 | % | |
| 4000 µm | 87.0 | % | |
| Haze (3000 µm) | < 0.80 | % | ISO 14782 |
| Note Message | |
|---|---|
| 1 . | Pellets |
| 2 . | 60x60x2 mm, 500 bar |
| 3 . | 60x60x2 mm, 500 bar |
| 4 . | 2.0 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 2 mm/min |
| 7 . | Based on ISO 179-1eA, 3 mm |
| 8 . | 3.2 mm |
| 9 . | 10°C/min |
| 10 . | Cross-flow |
| 11 . | Method A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rhelon G2918HU-01 | RheTech, Inc. | Nylon 66 | Rhelon |
| TECHNO MUH M3100 | Techno Polymer Co, Ltd. | ABS | TECHNO MUH |
| Toyolac® A20C-300 | Toray Resin Company | AS | Toyolac® |
| Pujie CPE-135C | Zhanhua Pujie Chemical Technology Co.,Ltd | CPE | Pujie |
| LNP™ THERMOCOMP™ PF00C compound | SABIC Innovative Plastics | Nylon 6 | LNP™ THERMOCOMP™ |