SABIC® LLDPE 726Q
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | I4dVpx_SABIC-LLDPE-726Q.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® LLDPE 726Q is a butene linear low density polyethylene resin. This grade is typically designed to give blown films a relatively high stiffness for good machinability and a good overall balance of other performance properties, such as puncture resistance, impact strength and heat sealability. This material contains anti block, slip erucamide and processing aid. Application Typical applications for SABIC® LLDPE 726Q are shipping sacks, produce bags, can liners and carrier bags. SABIC® LLDPE 726Q has good optical properties when blended with a LDPE (15-85%). This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.926 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.70 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Blown Film) | 0.10 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| MD : 50 µm, blown film | 220 | MPa | ISO 527-3 |
| TD : 50 µm, blown film | 240 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 50 µm, blown film | 13.0 | MPa | ISO 527-3 |
| TD : Yield, 50 µm, blown film | 14.0 | MPa | ISO 527-3 |
| MD : Broken, 50 µm, blown film | 34.0 | MPa | ISO 527-3 |
| TD : Broken, 50 µm, blown film | 27.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 50 µm, blown film | 600 | % | ISO 527-3 |
| TD : Broken, 50 µm, blown film | 700 | % | ISO 527-3 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Strength - Blown Film (50.0 µm) | 230 | J/cm | ASTM D4272 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Blocking - Blown Film (50.0 µm) | 10 | g | Internal method |
| Puncture Resistance - Blown Film (50.0 µm) | 440 | J/m | Internal method |
| Re-blocking - Blown Film (50.0 µm) | g | Internal method | |
| Tear Strength 1 | ISO 6383-2 | ||
| MD : 50.0 µm | 23.0 | kN/m | ISO 6383-2 |
| TD : 50.0 µm | 130.0 | kN/m | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 110 | °C | ISO 306/A |
| Melting Temperature (DSC) | 124 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm, Blown Film) | 65 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | 14 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film of 50 µm and BUR=2 has been produced on Kiefel IBC with 130 kg/h. Die size 200 mm, die gap 0.8 mm. |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AKROMID® B3 M 30 1 black (1831) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| Geon™ Vinyl Flexible A4DU6 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| GLS Acetal UN02 | GLS Polymers Pvt. Ltd. | Acetal (POM) Copolymer | GLS Acetal |
| TEDUR® L 9114-1 | ALBIS PLASTIC GmbH | PPS | TEDUR® |
| Sylvin 8785-80 White 1433 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |