Quantum Composites QC-2430
| Category: | Phenolic , Phenolic |
| Manufacturer: | Quantum Composites Inc. |
| Trademark: | Quantum Composites |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | I4Xewe_Quantum-Composites-QC-2430.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| QC-2430 is a glass-reinforced sheet molding compound based on a phenolic resin matrix. This exhibits the low flammability characteristics of phenolic resins plus resistance to very high temperatures. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.75 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.10 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 96.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.85 | % | ASTM D638 |
| Flexural Modulus | 10300 | MPa | ASTM D790 |
| Flexural Strength | 159 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 430 | J/m | ASTM D256 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Shelf Life (-18°C) | 26 | wk | |
| Post Cure Time (149°C) | 0.050 | hr |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 132 to 160 | °C | |
| Injection Pressure | 3.45 to 13.8 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Thermoplastic Polyolefin FT4802-693UV | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| Michicomp V10170 | API Polymers, Inc. | PVC, Unspecified | Michicomp |
| Chiao Fu PA66 MD312G23 BK | Chiao Fu Enterprises Co., Ltd. | Nylon 66 | Chiao Fu PA66 |
| LEXAN™ EX9332T resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |
| LUVOCOM® 1301-7399 VP | Lehmann & Voss & Co. | PPS | LUVOCOM® |