3M™ Dyneon™ PTFE TF 1620
| Category: | PTFE , Polytetrafluoroethylene |
| Manufacturer: | 3M Advanced Materials Division |
| Trademark: | 3M™ Dyneon™ PTFE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | I3C8ct_3M-Dyneon-PTFE-TF-1620.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Semi free-flowing PTFE for moulding with reduced pressure Features
Typical applications
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.15 | g/cm³ | ISO 12086 |
| Apparent Density | 0.87 | g/cm³ | ISO 60 |
| Molding Shrinkage | 2.9 | % | Internal Method |
| Average Particle Size | 220 | µm | ISO 13320 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 56 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 600 | MPa | DIN 53457 |
| Deformation Under Load | ASTM D621 | ||
| 15 MPa 1 | 10.0 | % | |
| 15 MPa 2 | 17.0 | % | |
| 15 MPa 3 | 16.0 | % |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (200 µm) | 38.0 | MPa | ISO 527-3 |
| Tensile Elongation (Break, 200 µm) | 400 | % | ISO 527-3 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE - Flow | DIN 53752 | ||
| 30 to 100°C | 1.2E-4 | cm/cm/°C | |
| 30 to 200°C | 1.7E-4 | cm/cm/°C | |
| 30 to 260°C | 1.4E-4 | cm/cm/°C | |
| Thermal Conductivity | 0.22 | W/m/K | DIN 52612 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+17 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+18 | ohms·cm | IEC 60093 |
| Electric Strength (0.200 mm) | 74 | kV/mm | ISO 12086 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | permanent |
| 2 . | 100 hr |
| 3 . | 24 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ESTAPROP H 05100GFC | Cossa Polimeri S.r.l. | PP Homopolymer | ESTAPROP |
| FRAGOM PR/6 AMR | Crosspolimeri S.p.A. | Polyolefin, Unspecified | FRAGOM |
| HiFill® PP 0254 S1 | Techmer Engineered Solutions | PP, Unspecified | HiFill® |
| Hyundai EP PA66 LD140 | HYUNDAI EP Co., Ltd. | Nylon 66 | Hyundai EP PA66 |
| MAJORIS BG300 | AD majoris | PP, Unspecified | MAJORIS |