TOPAS® 8007X-10

Category:	COC , Cyclic Olefin Copolymer
Manufacturer:	Topas Advanced Polymers, Inc.
Trademark:	TOPAS®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	I2ZylP_TOPAS-8007X-10.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Product Description
TOPAS 8007X10 is a highly UV-transparent version of our 8007 series of injection molding resins. Like the rest of the 8007 grades, 8007X10 is a glass-clear amorphous polymer with outstanding moisture barrier, chemical resistance, high purity and a non-reactive surface making it an excellent choice for diagnostic and analytical products. It transmits ultraviolet light at lower wavelengths than other polymers. Analytical results are more accurate with pure TOPAS COC and its higher UV transmission for more precise analysis in contact with sensitive chemistries.

Selected Applications

Cuvettes

Microplates

Biochips

Microfluidics

Optics

High purity applications

Healthcare and food contact

Leading Attributes

UV transparency at low wavelengths

Dimensional stability with UV transmission

Purity and chemical resistance

Exceptional mold detail replication; machinable

Clarity, low birefringence, low fluorescence

Not manufactured with BPA, phthalates, or halogens

Broad regulatory compliance

Related Grades for Injection Molding, Healthcare, Optics and Diagnostics

TOPAS 8007S-04 - standard grade, appropriate for most applications

TOPAS 8007D-61 - externally lubricated 8007S-04 for blow molding of bottles, vials, etc.

General Information
Features	Good dimensional stability High purity Moisture proof Copolymer Machinable Good chemical resistance Definition, high Compliance of Food Exposure BPA-free amorphous Halogen-free
Uses	Non-specific food applications Optical applications Medical/nursing supplies
Agency Ratings	DMF 12132 FDA FCN 405 Europe 10/1/2011 12:00:00 AM
Appearance	Clear/transparent
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.02	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (260°C/2.16 kg)	29	g/10 min	ISO 1133
Melt Volume-Flow Rate (MVR) (260°C/2.16 kg)	32.0	cm³/10min	ISO 1133
Molding Shrinkage ¹	0.10 - 0.30	%	Internal method
Water Absorption (Saturation, 23°C)	0.010	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	2600	MPa	ISO 527-2/1A/1
Tensile Stress (Yield)	63.0	MPa	ISO 527-2/1A/50
Tensile Strain (Yield)	4.5	%	ISO 527-2/1A/50

Films	Nominal Value	Unit	Test Method
Water Vapor Transmission Rate (23°C, 85% RH)	0.025	g·mm/m²/atm/24 hr	DIN 53122

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	3.0	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	20	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (0.45 MPa, Unannealed)	75.0	°C	ISO 75-2/B
Glass Transition Temperature	78.0	°C	ISO 11357-2
Vicat Softening Temperature	80.0	°C	ISO 306/B50

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity	> 1.0E+16	ohms·cm	IEC 60093
Relative Permittivity			IEC 60250
1 kHz	2.35		IEC 60250
10 kHz	2.35		IEC 60250
Comparative Tracking Index	> 600	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.60 mm)	HB		UL 94

Optical	Nominal Value	Unit	Test Method
Refractive Index	1.530		ISO 489
Transmittance	91.0	%	ISO 13468-2

Injection	Nominal Value	Unit
Drying Temperature	50.0	°C
Drying Time	4.0 - 6.0	hr
Rear Temperature	190 - 220	°C
Middle Temperature	200 - 240	°C
Front Temperature	220 - 250	°C
Nozzle Temperature	220 - 250	°C
Processing (Melt) Temp	190 - 250	°C
Mold Temperature	40.0 - 70.0	°C
Injection Pressure	50.0 - 110	MPa
Injection Rate	Moderate-Fast
Holding Pressure	30.0 - 60.0	MPa
Back Pressure	< 15.2	MPa
Screw Speed	50 - 200	rpm

Injection instructions
Feed temperature: <60°C (<140°F)Max. residence time: <15 minutes; short interruptions to cycle >10 minutes, reduce Tx = 170°C (338°F)Injection speed: 50 - 150 mm/sec (2.0 - 6.0 in/sec)Nozzle type: Free flow

Note Message
1 .	Dependent on processing conditions and part design.

Resin Grade	Manufacturer	Category	Trademark
SILVER® ABS 3360F	Guangdong Silver Age Sci & Tech. Co., Ltd	ABS	SILVER®
Ultradur® B 4330 G6 HR BK15045	BASF Corporation	PBT	Ultradur®
Karina WHITE PVC COMPOUND 808D10/173-C-IS	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
Sylvin 8200-93UV Clear Yellow 4194	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
ULTEM™ AUT195 resin	SABIC Innovative Plastics	PEI+PCE	ULTEM™