Cardia Biohybrid™ H-F

Category:	TPS+PE , Thermoplastic Starch + PE
Manufacturer:	Cardia Bioplastics™
Trademark:	Cardia Biohybrid™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	I2VwSD_Cardia-Biohybrid-H-F.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Cardia Biohybrid ™ H-F is a based on a blend of thermoplastic starch (TPS) with Polyethylene. This grade of resin is compatibilised to offer a high level of mechanical strength, elongation properties and toughness. The resin is based on corn starch which is a renewable material. A Biohybrid resin for film applications offering a significant reduction in carbon footprint (compared to PE) An effective contribution to sustainability where biodegradability/compostability is not required. Designed for thin and thick gauge film applications. Cardia Biohybrid™ H-F is formulated with 50% of annually renewable thermoplastic starch polymer. This resin is suitable for a range of products manufactured by blown film extrusion and extrusion blow molding as well as injection molding processes. Due its high content of polyolefins the material is not a fully biodegradable polymer and is not intended for ultimate disposal in commercial composting facilities. For applications in which compostability is required we recommend the usage of Cardia Compostable B-F resin. Application Examples Shopping bags/Check-out bags Garbage bags Leaf litter bags Bin liners Overwrap Packaging

Message

Cardia Biohybrid ™ H-F is a based on a blend of thermoplastic starch (TPS) with Polyethylene. This grade of resin is compatibilised to offer a high level of mechanical strength, elongation properties and toughness. The resin is based on corn starch which is a renewable material.

A Biohybrid resin for film applications offering a significant reduction in carbon footprint (compared to PE)

An effective contribution to sustainability where biodegradability/compostability is not required.

Designed for thin and thick gauge film applications.

Cardia Biohybrid™ H-F is formulated with 50% of annually renewable thermoplastic starch polymer. This resin is suitable for a range of products manufactured by blown film extrusion and extrusion blow molding as well as injection molding processes. Due its high content of polyolefins the material is not a fully biodegradable polymer and is not intended for ultimate disposal in commercial composting facilities. For applications in which compostability is required we recommend the usage of Cardia Compostable B-F resin.

Application Examples

Shopping bags/Check-out bags

Garbage bags

Leaf litter bags

Bin liners

Overwrap Packaging

General Information
Features	Food Contact Acceptable Good Toughness High Elongation High Strength Renewable Resource Content
Uses	Bags Blending Film Heavy-duty Bags Liners Packaging
Agency Ratings	EU 2002/72/EC
Processing Method	Blown Film Extrusion Blow Molding Injection Molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.10	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	1.0	g/10 min	ASTM D1238
Moisture Content	< 0.60	%	Internal Method

Additional Information	Nominal Value	Unit
Biobased Content - Starch	50	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength			ASTM D883
Yield	> 13.0	MPa
Break	> 13.0	MPa
Tensile Elongation (Break)	350	%	ASTM D883

Thermal	Nominal Value	Unit	Test Method
Peak Melting Temperature	90.0 to 130	°C	ASTM D3418

Resin Grade	Manufacturer	Category	Trademark
Royaltherm® 1411A	Lion Copolymer, LLC	EPDM	Royaltherm®
TRIBIT® 1500GN40	Samyang Corporation	PBT	TRIBIT®
Zhongfa ABS GR-10	Yuyao Zhongfa Engineering Plastics Co. Ltd.	ABS	Zhongfa
4MID® 9A22150 FRR1	4Plas	Nylon 66	4MID®
DESLON™ 66 DSC201G8	DESCO Co., Ltd.	Nylon 66	DESLON™ 66