EPLAMID 66 GFS 20 HS NC
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | EPSAN Plastik SAN. ve TiC. A.S. |
| Trademark: | EPLAMID 66 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | I2If5B_EPLAMID-66-GFS-20-HS-NC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polyamide 66, reinforced with 20% of glass fiber, heat stabilized, lubricated for injection moulding. Eplamid 66 GFS 20 HS is used in all sectors of industry, offering a perfect balance of thermal and mechanical properties. This product is available in natural and in colours on request. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.26 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction : 3.00mm | 1.1 | -- | % | ISO 294-4 |
| Flow direction : 3.00mm | 0.90 | -- | % | ISO 294-4 |
| Moisture Content | 0.20 | -- | % | ISO 15512 |
| Ash Content | 20 | -- | % | ISO 3451-4 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Durometer Hardness (Shore D, 23°C) | 87 | -- | ISO 868 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 7400 | 7100 | MPa | ISO 527-2/50 |
| Tensile Stress (Break, 23°C) | 140 | 125 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | 4.0 | 10 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 6900 | 6500 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 200 | 180 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | 11 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 8.0 | 9.0 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 3 | ||||
| 0.45 MPa, not annealed | 255 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 245 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 250 | -- | °C | ISO 306/B120 |
| Melting Temperature (DSC) | 250 | -- | °C | ISO 3146 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94, IEC 60695-11-10, -20 |
| Additional Information |
|---|
| 干燥 TEST CONDITIONS: Laboratory conditions are 23 ±2°C and 45-55 % RH. |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 280 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 120°C/h |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RELENE® 1005FY20 | Reliance Industries Limited | LDPE | RELENE® |
| Sindustris PP TE5109H | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| AIE PBT 30G8 | Asia International Enterprise (Hong Kong) Limited | PBT | AIE PBT |
| HAIPLEN H10 G6 BA | Taro Plast S.p.A. | PP Homopolymer | HAIPLEN |
| TECHNYL® A 218HPS V50 BLACK 21N | Solvay Engineering Plastics | Nylon 66/6 | TECHNYL® RED |