ULTEM™ ATX200 resin
| Category: | PEI , Polyether Imide + PCE |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | I1vmzT_ULTEMATX200resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High flow Polyetherimide blend. RoHS compliant, UL94 V0 Listing. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.26 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 24 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (340°C/5.0 kg) | 16.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Flow 1 | 0.50 - 0.70 | % | Internal method |
| Flow : 3.20mm | 0.50 - 0.70 | % | Internal method |
| Transverse flow : 3.20mm | 0.50 - 0.70 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.90 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.50 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 125 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 3300 | MPa | ASTM D638 |
| -- | 3000 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 3 | 97.0 | MPa | ASTM D638 |
| Yield | 95.0 | MPa | ISO 527-2/50 |
| Fracture 4 | 85.0 | MPa | ASTM D638 |
| Fracture | 75.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 5 | 7.0 | % | ASTM D638 |
| Yield | 6.5 | % | ISO 527-2/50 |
| Fracture 6 | 70 | % | ASTM D638 |
| Fracture | 20 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 7 | 3170 | MPa | ASTM D790 |
| -- 8 | 3100 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 125 | MPa | ISO 178 |
| Yield, 50.0mm span 9 | 145 | MPa | ASTM D790 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 20.0 | mg | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 10 | ISO 179/1eA | ||
| -30°C | 4.0 | kJ/m² | ISO 179/1eA |
| 23°C | 4.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 55 | J/m | ASTM D256 |
| 23°C | 53 | J/m | ASTM D256 |
| -30°C 11 | 5.0 | kJ/m² | ISO 180/1A |
| 23°C 12 | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | 2100 | J/m | ASTM D4812 |
| Reverse Notch Izod Impact (3.20 mm) | 2700 | J/m | ASTM D256 |
| Instrumented Dart Impact (23°C, Total Energy) | 50.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, unannealed, 100 mm span 13 | 195 | °C | ISO 75-2/Be |
| 1.8 MPa, unannealed, 3.20mm | 187 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 191 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 100 mm span 14 | 180 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 209 | °C | ASTM D1525 15 |
| -- | 210 | °C | ISO 306/A50 |
| -- | 200 | °C | ISO 306/B50 |
| -- | 205 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 150°C | 5.0E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 150°C | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 150°C | 5.0E-5 | cm/cm/°C | ASTM E831 |
| Horizontal : 23 to 150°C | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.23 | W/m/K | ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 2.90 | IEC 60250 | |
| 60 Hz | 2.90 | IEC 60250 | |
| 1 MHz | 2.90 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 1.0E-3 | IEC 60250 | |
| 60 Hz | 1.0E-3 | IEC 60250 | |
| 1 MHz | 5.0E-3 | IEC 60250 | |
| Comparative Tracking Index | 150 | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | PLC 4 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-2 | UL 94 | |
| 1.50 mm | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 130 - 140 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Hopper Temperature | 80.0 - 100 | °C | |
| Rear Temperature | 320 - 340 | °C | |
| Middle Temperature | 330 - 350 | °C | |
| Front Temperature | 340 - 360 | °C | |
| Nozzle Temperature | 340 - 360 | °C | |
| Processing (Melt) Temp | 340 - 380 | °C | |
| Mold Temperature | 125 - 140 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | Type 1, 5.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 sp=62mm |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 |
| 13 . | 120*10*4 mm |
| 14 . | 120*10*4 mm |
| 15 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Network Polymers PP PPH 30 2000 | Network Polymers, Inc. | PP Homopolymer | Network Polymers PP |
| CABELEC® CA3839 | Cabot Corporation | PP Copolymer | CABELEC® |
| Ebalta ebatemp / PUR 5 | Ebalta Kunststoff GmbH | PUR, Unspecified | Ebalta |
| EnCom ABS 5025 | EnCom, Inc. | ABS | EnCom |
| Sylvin 9940-75 NATURAL | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |