Clariant Nylon 6 PA-211CF30 TF15

Category:	Nylon 6 , Polyamide 6
Manufacturer:	Clariant Corporation
Trademark:	Clariant Nylon 6
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	I1GhiG_Clariant-Nylon-6-PA-211CF30-TF15.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Clariant Nylon 6 PA-211CF30 TF15 is a polyamide 6 (nylon 6) material, which contains a 30% carbon fiber reinforced material. This product is available in North America and is processed by injection molding.

The main features of Clariant Nylon 6 PA-211CF30 TF15 are:

flame retardant/rated flame

Flame Retardant

Conductivity

high strength

Good processability

Typical application areas include:

Wire and cable

military applications

business/office supplies

Sporting goods

medical/health care

General Information
Filler / Reinforcement	Carbon fiber reinforced material, 30% filler by weight
Additive	PTFE lubricant (15%)
Features	Good dimensional stability Conductivity Low friction coefficient Rigidity, high Rigid, good High strength Workability, good Good corrosion resistance Good coloring Good chemical resistance Good wear resistance Good toughness Lubrication Flame retardancy
Uses	Metal substitution Military application Business equipment Sporting goods Medical/nursing supplies
Agency Ratings	UL 94
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.37	g/cm³	ASTM D792
Molding Shrinkage - Flow (3.18 mm)	0.25	%	ASTM D955
Water Absorption (24 hr)	0.70	%	ASTM D570

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness			ASTM D785
Class m	88		ASTM D785
Class r	123		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength	210	MPa	ASTM D638
Tensile Elongation (Break)	2.0	%	ASTM D638
Flexural Modulus	14500	MPa	ASTM D790
Flexural Strength	290	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (3.18 mm)	53	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load			ASTM D648
0.45 MPa, not annealed	216	°C	ASTM D648
1.8 MPa, not annealed	213	°C	ASTM D648
CLTE - Flow	1.8E-5	cm/cm/°C	ASTM D696

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity	1.0E+3	ohms·cm	ASTM D257

Flammability	Nominal Value	Unit	Test Method
Flame Rating	HB		UL 94

Injection	Nominal Value	Unit
Drying Temperature	79.4	°C
Drying Time	2.0 - 4.0	hr
Suggested Max Moisture	0.20	%
Rear Temperature	249 - 274	°C
Middle Temperature	249 - 274	°C
Front Temperature	249 - 274	°C
Processing (Melt) Temp	254 - 271	°C
Melt Temperature (Aim)	266	°C
Mold Temperature	65.6 - 93.3	°C
Injection Rate	Fast
Back Pressure	0.345 - 0.689	MPa
Screw Speed	20 - 100	rpm
Cushion	3.18 - 6.35	mm

Injection instructions
Injection Pressure: Use minimum pressure to achieve 95% fill during the boost inj. pressure phase.Hold Pressure: 30% to 75% of injection pressure.Mold Temp. Target: 180°FScrew Speed Target: 75 RPM

Resin Grade	Manufacturer	Category	Trademark
SNOLEN® EF 3.3/54	JSC Gazprom neftekhim Salavat	HDPE	SNOLEN®
Titalon® 2330GF	Titan Plastics Compounds Co., Ltd.	Nylon 66	Titalon®
ALCOM® PC 740/4 RD1451-06LD	ALBIS PLASTIC GmbH	PC	ALCOM® PC
Alpha PVC 2212C2B/H-118 CLEAR 0003	AlphaGary	PVC, Rigid	Alpha PVC
HAIPLEN H50 C12	Taro Plast S.p.A.	PP Homopolymer	HAIPLEN