TECHNYL® C 216 V40 BLACK Z
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® C |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | I0BxtL_TECHNYL-C-216-V40-BLACK-Z.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYL® C 216 V40 Black Z is a polyamide 6, reinforced with 40% of glass fibre, for injection moulding. This product is available in black color. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.45 | -- | g/cm³ | ISO 1183/A |
| Water Absorption (23°C, 24 hr) | 0.90 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 13100 | 7300 | MPa | ISO 527-2/1A |
| Tensile Stress (Break) | 215 | 140 | MPa | ISO 527-2/1A |
| Tensile Strain (Break) | 2.3 | 3.5 | % | ISO 527-2/1A |
| Flexural Modulus | 13000 | 7200 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 18 | 34 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 110 | 120 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength (23°C) | 16 | 29 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 214 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 222 | -- | °C | ISO 11357-3 |
| Peak Crystallization Temperature | 190 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+11 | ohms·cm | IEC 60093 |
| Electric Strength | -- | 22 | kV/mm | IEC 60243-1 |
| Dissipation Factor | 0.020 | 0.090 | IEC 60250 | |
| Comparative Tracking Index | IEC 60112 | |||
| Solution A | 600 | 600 | V | |
| Solution B | 475 | -- | V |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.400 mm | HB | -- | ||
| 0.800 mm | HB | -- | ||
| 1.60 mm | HB | -- | ||
| 3.20 mm | HB | -- | ||
| Glow Wire Flammability Index (1.60 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 225 to 230 | °C | |
| Middle Temperature | 230 to 240 | °C | |
| Front Temperature | 245 to 255 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Niche PPHG30BK | Niche Polymer, LLC | PP Homopolymer | Niche |
| Novamid® 1013J | DSM Engineering Plastics | Nylon 6 | Novamid® |
| KRATON® D1119 B | Kraton Polymers LLC | SIS | KRATON® |
| POLYFORT® FPP 20 GFC | A. Schulman Europe | PP Homopolymer | POLYFORT® |
| LEXAN™ OQ2720 resin | SABIC Innovative Plastics | PC | LEXAN™ |