Xytron™ M6510A
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Xytron™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | I08cHw_XytronM6510A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Xytron™M6510A is a polyphenylene sulfide (PPS) material, which contains 65% glass \minerals. This product is available in the Asia-Pacific region,. Xytron™The main characteristics of M6510A are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.97 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 0.40 | % | ISO 294-4 |
| Flow | 0.20 | % | ISO 294-4 |
| Water Absorption (Saturation, 23°C) | 0.020 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ISO 2039-2 | ||
| M scale | 101 | ISO 2039-2 | |
| R scale | 120 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2 | ||
| -- | 21000 | MPa | ISO 527-2 |
| 120°C | 11400 | MPa | ISO 527-2 |
| 160°C | 8500 | MPa | ISO 527-2 |
| 200°C | 5500 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Fracture | 150 | MPa | ISO 527-2 |
| Fracture, 120°C | 98.0 | MPa | ISO 527-2 |
| Fracture, 160°C | 70.0 | MPa | ISO 527-2 |
| Fracture, 200°C | 58.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Fracture | 1.0 | % | ISO 527-2 |
| Fracture, 120°C | 1.6 | % | ISO 527-2 |
| Fracture, 160°C | 2.2 | % | ISO 527-2 |
| Fracture, 200°C | 3.8 | % | ISO 527-2 |
| Flexural Modulus | ISO 178 | ||
| -- | 20000 | MPa | ISO 178 |
| 120°C | 14000 | MPa | ISO 178 |
| 160°C | 9100 | MPa | ISO 178 |
| 200°C | 7000 | MPa | ISO 178 |
| Flexural Stress | 230 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 7.3 | kJ/m² | ISO 179/1eA |
| 23°C | 7.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 27 | kJ/m² | ISO 179/1eU |
| 23°C | 25 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 260 | °C | ISO 75-2/A |
| Melting Temperature 1 | 280 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 1.5E-5 | cm/cm/°C | ISO 11359-2 |
| Flow 2 | 2.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 2.4E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral 3 | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | 20 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 225 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 0.70 mm | V-0 | IEC 60695-11-10, -20 | |
| 1.5 mm | V-0 | IEC 60695-11-10, -20 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 120 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 300 - 320 | °C | |
| Middle Temperature | 310 - 330 | °C | |
| Front Temperature | 320 - 340 | °C | |
| Nozzle Temperature | 310 - 340 | °C | |
| Processing (Melt) Temp | 310 - 340 | °C | |
| Mold Temperature | 130 - 150 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 - 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | above Tg |
| 3 . | above Tg |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNO MUH LG5053 | Techno Polymer Co, Ltd. | ABS | TECHNO MUH |
| Nanjing Hongrui PA66 A401 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 66 | Nanjing Hongrui PA66 |
| Abstron IMC45 FR V2 | Bhansali Engineering Polymers Limited | PC+ABS | Abstron |
| DIC.PPS Z-230 | DIC Corporation | PPS | DIC.PPS |
| Sylvin 9077-88 Grey 9462 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |