Infino VB-5150GL
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HzeeOq_Infino-VB-5150GL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino VB-5150GL is a Polybutylene Terephthalate (PBT) product filled with glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.54 | g/cm³ | ASTM D792 |
| -- | 1.53 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 21 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 1.1 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.070 | % | ASTM D570 |
| Ash Content | |||
| -- | 15 | % | ISO 3451 |
| -- | 15 | % | ASTM D5630 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale | 118 | ASTM D785 | |
| R-Scale | 120 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4600 | MPa | ASTM D638 |
| -- | 5200 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 83.0 | MPa | ASTM D638 |
| Yield | 98.0 | MPa | ISO 527-2/50 |
| Break 3 | 82.0 | MPa | ASTM D638 |
| Break | 98.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 4 | 3.3 | % | ASTM D638 |
| Break | 3.1 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 5800 | MPa | ASTM D790 |
| -- 6 | 5200 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 150 | MPa | ASTM D790 |
| -- 8 | 134 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 2.8 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 28 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 33 | J/m | ASTM D256 |
| 23°C 10 | 2.8 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 214 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 4.00 mm | 210 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 194 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 179 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 202 | °C | ISO 306/B50 |
| -- | 206 | °C | ISO 306/B120 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.740 mm | V-0 | ||
| 1.70 mm | V-0 | ||
| 3.00 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 100 | °C | |
| Desiccant Dryer | 100 | °C | |
| Drying Time | |||
| -- | 4.0 to 6.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 210 to 220 | °C | |
| Middle Temperature | 225 to 230 | °C | |
| Front Temperature | 240 to 250 | °C | |
| Nozzle Temperature | 250 | °C | |
| Mold Temperature | 60.0 to 120 | °C | |
| Injection Pressure | 49.0 to 245 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4 mm |
| 10 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ferro PP NPP00GD14NA | Ferro Corporation | PP Copolymer | Ferro PP |
| EPOPLEN PP CFR 10 NC | EPSAN Plastik SAN. ve TiC. A.S. | PP, Unspecified | EPOPLEN |
| Braskem PP TI4360P3 | Braskem America Inc. | PP Impact Copolymer | Braskem PP |
| KMI PE LDPE REPRO | KMI Group, Inc. | LDPE | KMI PE |
| Sylvin 8631-90 Clear 876 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |