Compound based on Polycarbonate (PC). Carbon fibre. Low smoke toxicity index and optical density. Fair dimensional stability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.28 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.20 to 0.35 | % | |
| Flow : 2.00 mm | 0.10 to 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 12000 | MPa | |
| 60°C | 11500 | MPa | |
| 90°C | 10500 | MPa | |
| 120°C | 9400 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Break, 23°C | 130 | MPa | |
| Break, 60°C | 110 | MPa | |
| Break, 90°C | 90.0 | MPa | |
| Break, 120°C | 65.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Break, 23°C | 1.7 | % | |
| Break, 60°C | 1.6 | % | |
| Break, 90°C | 1.6 | % | |
| Break, 120°C | 1.7 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 30 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C, 3.20 mm) | 85 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 140 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 135 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 135 | °C | |
| Vicat Softening Temperature | 145 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 2.5E-6 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 130 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 100 to 120 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Fainplast PVC GS 75/R1 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Formolene® L62009H | Formosa Plastics Corporation, U.S.A. | LLDPE | Formolene® |
| ALCOM® PC 740/4 UV WT1296-07LD | ALBIS PLASTIC GmbH | PC | ALCOM® PC |
| Sylvin 3240-55 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LUVOCOM® 1105-0904/GN | LEHVOSS Group | PEEK | LUVOCOM® |